D0I:10.13374/j.issm1001-053x.1991.02.005 第13卷第2期 北京科技大学学报 Vol.13 No,2 1991年3月 Journal of University of Science and Technology Beijing March 1991 加筋复合白口铁的强韧化及断裂方式 赵爱民·王兆昌· 摘要：研究了加筋式复合白口铁的机械性能、强韧化机理及其断裂方式。实验结果表 明：加筋复合白口铁的机械性能优于单一的白口铁，其抗弯强度及冲击韧性随钢筋的体积分 数的增加而增加，在合适的钢筋体积分数时强韧化效果最好。对复合白口铁的冲击试样的断 口进行SEM观宾，发现复合白口铁中钢筋有3种断裂方式，即完全脆性断裂、部分脆性断 裂和韧性断裂，它们影响复合白口铁的强度和冲击韧性。 关键词：白口铁，复合材料，锅筋强化，韧化 Strengthening,Toughening and Fracture Behavior of Composite White Cast Iron Zhao Aimin Wang Zhaochang' ABSTRACT:The strengthening,toughening and fracture behavior of composite white cast iron which was composed of reinforcement steel bar and white cast iron have been researched.The results of bend tests and impact tests of specimens of composite white cast iron indicated that the bending strength and impact toughness of it were superior to those of straight white cast iron. The improvements of bending strength and impact toughness were related to the volume fraction of reinforcement bar.Three fracture modes of steel bar in composite white cast iron were found by examining the surfaces of fracture by SEM.Those were brittle fracture,ductile fracture and mixed fra- 1990-10-13收稿 ·治金系(Department of Metallurgy) 123第 卷第 期 年 月 北 京 科 技 大 学 学 报 。 。 。 加筋复合白口 铁的强韧化及断裂方式 赵爱民 ， 王兆 昌 ， 摘 要 研究了加筋式 复合白口 铁的 机械性能 ， 强 韧化 机理 及其断裂 方式 。 实脸 结 果 表 明 加筋 复合白口 铁的机械性能优于单一 的白 口 铁 ， 其抗弯强 度及冲击 韧性随钢舫的体积分 数的增加而增加 ， 在合适的钢 筋体积分数时强 韧化效 果最好 。 对 复合 白口 铁的 冲击 试样的断 口 进行 观察 ， 发现 复合白口 铁中钢 筋有 种断 裂方式 ， 即完全脆性断裂 、 部分脆性断 裂和韧性断裂 ， 它们影响 复合 白 口铁的强度和冲击韧性 。 关挂词 白口 铁 ， 复合材料 ， 铜筋弧 化 ， 切化 、 ， 平 夕 夕 ， 五 。 五 五 。 。 ， 一 一 收稿 冶金系 DOI ：10．13374／j ．issn1001－053x．1991．02．005