五、结 论 1.RE氧化物固态渣饼作为脱S剂和变质剂，在铸造铁水的温度范围内，在吹Ar和周 态渣条件下，对高硫铁水的变质处理，在理论上是可行的，在实验室规模下是成功的。 2.提高变质处理的温度和降低处理过程的Pco都能缩短高硫铁水变质处理的时间。 3.在过共晶铁小条泮下，当RE%≤(CE%-4.306)/25时可获得螺铁。蹴铁中 RE%残量波动范圈为0.006~0.038%。当RE%≥(CE%-4.30%)/25时可以获得球铁。 主要参考文献 〔1)朱元凯彭育强洪彦若李联生扬广禄稀土、4（1983)9. 〔2)朱元凯彭育强于学斌苏留记中国稀土学报2.1(1984)67. 〔3)朱元凯彭育强洪彦若苏留记于学斌金属学报23.4(B)(1984)167 (4)Mickelson,R.L.,Modern Castings 54 N0 3 (1958)95. (5)Compomanes,E.Galler,R.AFS Trans (1975)55. (6)Vahed,A.and Kay,D.A.R.Met trans 7B (1976)375. 〔7)魏寿昆冶金过程热力学上海科技出版社(1980)6. Investigation of Modifying Treatment with Rare-Earth Oxide for High-sulphur Moltem Peng Yuqiang,Li Lifen.Li Liansheng Zhu Yuankai. Abstract Applying solid slag Cakes of rare earth oxide as a desulphurizinga gent as well as a modifying agent and under Condition of Ar-blowing,a hy- pereutictic hot metal of high Sulphur content (s=0.100%)has been mo- difyied.Experiments are made at 1450c for about 30~35 minutes. Changeing laws of chemical composition in hot metal and relationship between graphite morphogy and contentof RE,CE in casting are abta- ined.Results indicate that the RE%<(CE%-4.30%)/25 and the RE%> (CE%-4.30%)/25 canbe abtained vermicalar cast iror and nodular cast iron respectively under hypereutectic hot metal.with regrad to disuph- urizing reaction and redwction reaction of rare earth oxrde,discussion and thermodynamic calculation have been Carried out.The results point out that the above mentioned reaction are all established thermodyra- mically umder the experimental condition. 86五 、 结 论 氧 化物固态渣饼作为脱 剂和变质剂 ， 在铸造铁水 的温度 范围 内 ， 在吹 和 固 态 渣条件下 ， 对高 硫铁水 的变 质处理 ， 在 理论 上是可 行 的 ， 在 实验室 规模下 是 成功 的 。 提 高 变 质处 理的 温度和 降低 处理 过程 的 。 。 都 能缩 短高 硫铁 水变质 处 理 的 时 间 。 在过共 晶 铁 水 条 斗 下 ， 当 一 乡‘ 〕 时 可 获得 蠕铁 。 蠕 铁 中 残量 波 动 范围 为 。 当 一 石 时可 以 获得球 铁 。 主 要 今 考 文 献 〔 〕 〔 〕 〔 〕 〔 〕 〔 〕 〔 〕 〔 〕 朱 元 凯 彭育强 洪彦若 李联生 扬广 禄 稀 土 、 朱 元 凯 彭 育 强 于 学斌 苏 留记 中国稀 土学 报 朱 元 凯 彭 育强 洪彦若 苏 留记 于学 斌 金属学 报 ， ， 地 ， ， ， ， ， 了 魏 寿昆 冶金过程热力学 上海 科技 出版社 一 一 ， 一 ， 一 二 一 ℃ · ， 三 一 七 一 已 。 。 一 ， 一