D0I:10.13374/j.issnl001-053x.1987.s1.011 北京钢铁学院学报 Journal of Beijing University Special issue of Iron and Steel Technology No.21987.6 FGH95合金粉末表面和颗粒间界的 化学成分及析出相 吳承建 李景慧 冯松筠 章守华 (金相敦研室) 要 用TEM+EDAX和AES分析了FGH95粉未颗粒表而和等静压坏的颗粒间界的化学成分及析出相。结 果表明：氢气雾化粉未属粒表面硫、氧、碳、钛的含量较高，並有TC相析出。等静压后撕粒间界的碳化物 是言银的Nb、Ti、MO)C,衡粒间界硫和氧的含量大大降低，等静过程中有少量磷向颗粒边界偏聚。 Chemical Composition and Precipitates at the Particle Surface and Primary-particle Boundaries of HIPed FGH95 Alloy Wu Chengjian Li Jinhui Feng Songyun Zhang Shouhun Abstract By means of TEM,TEDAX and AES the chemical composition and pre- cipitates on particle surface and at the primary particle/particle boundaries of HIPed billet have been investigated,Experimental results show that the particle surface of powders produced by Ar atomisation is enriched with S,C,Ti.O and Tic particles also precipitate on the surface.After hot isostatic pressing, the carbides distributed around the primary-particle boundaries are niobium ri- ched (Nb,Ti,Mo)C phase,S and o concentration drastically decreases at the primary-particle boundaries,and a small amount of P segregate to the pri- mary-particle boundaries during hot isostatic pressing. 81北 京 钢 铁 学 院 学 报 ， 二 ‘ 二二二孟二二盆二 屯‘ 二于 二之气黔冲忿 尸 ，，口二二 之二二二二二二二 二 卞 。 合金粉末表面和颗粒 间界的 化学成分及析出相 吴承建 李景 慧 冯松药 章守华 金相教 研室 摘 要 用 和 分析了 粉末城 拉 表面 和 等 朴压 坏 的顶粒间 界的化 学成 分及 析 出相 。 结 果表明 姐气雾化粉末城拉表面 硫 ， 氧 、 碳 、 钱的含全较 高 ， 业有 相析 出 等静压 后城 粒 间 界的碳 化 物 是二银的 、 、 ， 城 粒间 界硫和 长的含 吸大 大 降低 等 静压 过 程 中有少 磷向 箱较 边界 偏聚 。 门 口 一 “ ，” 万 泣 “ 尸 刀 污 夕 几 ” 夕几。 “ 几“ 人 口 ， 加 。 、 、 、 ， 一 、 ， ， 一 ， 了 一 乓 ， 落 ， DOI ：10．13374／j ．issn1001－053x．1987．s1．011