D0I:10.13374/i.issn1001053x.1992.02.015 第14卷第2期 北京科技大学学报 Vol,14 No.2 1992年3月 Journal of University of Science and Technology Beijing March 1992 应力腐蚀机理研究 褚武扬·乔利杰*肖纪美* 摘要：本文提出必须综合电化学、碰活能、加载方式、门槛值、裂纹形核位置以及断 口形貌的对比研究，压应力产生裂纹可能性以及裂纹形核和局部塑性变形关系的研究才能确 定应力鹰蚀机理是属于阳极溶解型还是氢致开裂型。不锈钢在热盐溶液中应力腐蚀时氢能进 入并富集，且能加速应力魔蚀，但它不起控制作用，故属于阳极溶解型。氢和应力对阳极溶 解有协同作用对阳极溶解型应力腐蚀，正应力起了控制作用。 关键词：应力腐蚀，氢致开裂，阳极溶解 Research about Mechanism of Stress Corrosion Cracking' Chu Wuyang'Qiao Liji,Xiao Jimei ABSTRACT:That stress corrosion cracking (SCC)is belong to hydrogen induced cracking (HIC)or the anodic preferential dissolution can be solved based on a synthetical study using the following methods,i.e,electrochemistry,the activation energy,the effect of loading modes,comparing the threshold value,initiation site and fracture of SCC to these of HIC,cracking initiation under compressive stress and the correiation between the local plastic deformation and crack nucle- ation,During SCC of austenitic stainless steel in MgCIz solution,hydrogen can enter into the specimen and enrich and then facilitate the anodic dissolution but 十国家自然科学基金资助项目 1991-08-15收稿 ·材料物理系(Dcpt.of Matcrials Physics 2124 第 卷第 期 2 1 3 9 9 年 月2 1 北 京 科 技 大 学 学 报 J u r n a o l o f U n v i r e s y t i o S f e i n n ea e e T d e e h n o l o g B y e i j i n g V o l 。 4 1 N o . 2 M r a e 99 2 1 h 应力腐蚀机理研究 ` 褚武扬 ` 乔利杰 , 肖纪 美 , 摘 要 : 本文提出必须缭合电化学 、 激活能 , 加载方式 、 门槛值 、 裂纹形核 位置以及断 口 形貌的对比 研究 , 压 应力产生裂纹可能性以及裂纹形核和局部 塑性变形关 系的研究才能 确 定应力腐 蚀机理是属于阳极溶解型还是氢致开裂型 。不锈钢在热盐溶 液中应力腐蚀时氢 能进 人并富集 , 且能 加速应力腐蚀 , 但它不 起控 制作 用 , 故属于 阳极溶 解型 。 氢和应力对 阳极 溶 解 有协同作 用 。对 阳极溶 解型 应力腐蚀 , 正 应力 起 了控制作 用 。 关健词: 应力腐蚀 , 氢致 开裂 , 阳极溶 解 , , . R e s e a r e h a b o u t M e e h a n i s m o f S t r e s s C o r r o s i o n C r a e k i n g + C h “ 牙 u y a n g . Q f a o L i j f ` X ` a o J f 加 e 犷 ` A B S T R A C T : T h a t s t r e s s e o r r o s i o n e r a e k i n g ( S C C ) 1 5 b e l o n g t o h y d r o g e n i n d u e e d e r a e k i n g ( H I C ) o r t h e a n o d i e p r e f e r e n t i a l d i s s o l u t i o n e a 妞 b e s o l v e d b a s e d o n a s y n t h e t i e a l s t u d y u s i n g t h e f o l l o w i n g m e t h o d s , i 。 e , e l e e t r o e 五e m i s t r y , t h e a e t i v a t i o n e n e r g y , t h e e f f e e t o f l o a d i n g m o d e s , e o tn p a r i n g t h e t h r e s h o l d v a l u e , i n i t i a t i o n s i t e a n d f r a e t u r e o f S C C t o t h e s e o f H I C , e r a e k i n g i n i t i a t i o n u n d e r e o m p r e s s i v e s t r e s s a n d t h e e o r r e i a t i o n b e t w e e n t h e l o e a l P l a s t i e d e f o r m a t i o n a n d e r a e k n u e l e - a t i o n . D u r i n g S C C o f a u s t e n i t i e s t a i n l e s s s t e e l i 几 M g C I : s o l u t i o n , h y d r o g e n e a n e n t e r i n t o t h e s p e e i m e n a n d e n r i e h a n d t h o n f a e i li t o t e t卜e a n o d i e d i s s o l u t i o n b u t 十 国家白然科 学基金资助项 目 1 9 9 1 一 0 5 一 15 收稿 , 材料物 理系 ( D e P t . o f M a t e r i o l s p h y s 策c s 2 12 DOI: 10. 13374 /j . issn1001 -053x. 1992. 02. 015