D0I:10.13374/i.issm1001053x.1992.03.031 北京科技大学学报 第14卷第3期 Vo1.14No.3 1992年5月 Journal of University of Science and Technology Beijing May 1992 氢致304L不锈钢晶体结构变化与相变 高佳·谢逸凡· 肖纪美· 摘要：利用X射线行射方法，研究了30L不锈钢中电解充氢过程和随后时效过程中的 氢致奥氏体结构变化和氢致马氏体相变。结果表明，电解充氢可导致奥氏体晶格膨胀和马氏 体相变，《'相和相同时出现，并且在案温时效过程中并不能消失。 关健词：氢脆，X射线行射，马氏体相变 Hydrogen Induced Structure and Phase Transformation in 304L Stainless Steel Gao Jia Xie Yifan'Xiao Jimei. ABSTRACT:Hydrogen induced austenite structure transformation and martensite transformation in 304L stainless steel during hydrogen charging and aging were studied by X-ray diffraction.The results showed that hydrogen charging could induce austenite lattice expansion and martensite transformation,a'phase and e phase appeared in the same time,and they did not disappear after aging at room temperature, KEY WORDS:hydrogen embrittlement,X-ray diffraction,martensite transformation 关于304L奥氏体不锈钢在充氢与时效过程中晶体结构变化、相变机理的研究，前人已 做过大量的工作，但得到的试验结果与看法却很不相同。Eliezer D1)报道：304L不锈钢 在充氢24h后有e,a马氏体生成，相变顺序为y→e+a'而Shimizu2则报导了a'马氏体是 1991-10-24收搞 +本课题为国家自然科学基金资助项目 材料物班系(Deparment of Materials Physics) 368第 卷第 期 年 月 北 京 科 技 大 学 学 报 亡 。 氢致 不锈钢晶体结构变化与相变 ‘ 高 佳 ’ 谢 逸凡 ’ 肖纪 美 ’ 摘 要 利用 射线衍射方法 ， 研究 了 。 、 不 锈 钢中电解充氢过程和 随后时效过程 中的 氢致 奥氏体结构变化和氢 致马 氏体相变 。 结 果表明 ， 电 解充氢可 导致奥 氏体晶格膨胀和 马 氏 体相 变 ， 产相和亡相 同时 出现 ， 并且在室 温时 效过 程 中并不 能消失 。 关健词 氢 脆 ， 射 线衍射 ， 马 氏体相 变 了 ‘ ， 一 尹 ， 、 ， 一 ， 关于 奥 氏体不 锈钢在充氢与 时 效 过程 中晶体结 构变化 、 做过大量的工 作 ， 但得到的 试验结果与 看法 却 很不相 同 。 相 变机理 的 研究 ， 前 人 已 〔 ‘ ’ 报道 不锈钢 在充氢 后 有。 ， ， 马 氏体 生 成 ， 相 变顺序 为 夕。 ‘ 而 〔 “ ’ 则 报导 了’ 马 氏体是 一 一 收稿 十 本课题为国家 自然科学墓金资助 项 目 材料物 理 系 产 DOI ：10．13374／j ．issn1001－053x．1992．03．031