MIL-HDBK-17-2F Volume 2,Chapter 4 Carbon Fiber Composites DATA WERE SUBMITTED BEFORE THE ESTABLISHMENT OF DATA DOCUMENTATION REQUIREMENTS (JUNE 1989).ALL DOCUMENTATION PRESENTLY REQUIRED WERE NOT SUPPLIED FOR THIS MATERIAL. Nominal As Submitted Test Method Fiber Density (g/cm) 1.79 Resin Density (g/cm) 1.28 Composite Density (g/cm3) 1.59 1.57.1.61 Fiber Areal Weight (g1m3) 142 142-146 Fiber Volume (%) Ply Thickness (in) 0.0053 0.0050-0.0057 LAMINATE PROPERTY SUMMARY Classes of data in Strength/Modulus/Poisson's Ratio/Strain-to-Failure order:A A75,a =A55,B=B30,b B18, M Mean,I Interim,s Screening,-=no data (See Table 1.4.2(c)) 4-3MIL-HDBK-17-2F Volume 2, Chapter 4 Carbon Fiber Composites 4-3 ∗ DATA WERE SUBMITTED BEFORE THE ESTABLISHMENT OF DATA DOCUMENTATION REQUIREMENTS (JUNE 1989). ALL DOCUMENTATION PRESENTLY REQUIRED WERE NOT SUPPLIED FOR THIS MATERIAL. Nominal As Submitted Test Method Fiber Density (g/cm3 ) 1.79 Resin Density (g/cm3 ) 1.28 Composite Density (g/cm3 ) 1.59 1.57 - 1.61 Fiber Areal Weight (g/m2 ) 142 142 - 146 Fiber Volume (%) Ply Thickness (in) 0.0053 0.0050 - 0.0057 LAMINATE PROPERTY SUMMARY Classes of data in Strength/Modulus/Poisson’s Ratio/Strain-to-Failure order: A = A75, a = A55, B = B30, b = B18, M = Mean, I = Interim, S = Screening, - = no data (See Table 1.4.2(c))