Vol.18 No.5 王岚等：单晶金刚石在铁基合金中的性态与行为 ·431· 能的损失或失效.因此，适当控制C原子的扩散和扩散失活，才能够保证F基金刚石工具 的优良性能. 4结论 (I)F基合金对单晶金刚石的中度刻蚀，不导致金刚石晶体的结构转变及强度变化. (2)F基合金（结合剂）对金刚石的刻蚀在金刚石与结合剂的界面发生，是金刚石晶格中 的C原子溶入Fe并在其中扩散的过程. (3)适当控制C原子扩散和C原子的扩散失活，有可能获得性能优良的F基金刚石工 具 参考文献 1 Ralchenko V G.Kononenko T V.Catalytic Interaction of Fe,Ni and Pt with Diamond Films: Patterning Application.Diamond and Related Materials,1993(2):904~909 2 Jin S,Graebner J E.Massive Thinning of Diamond Films by A Diffusion Process.Appl Phys Lett, 1992,60(16):20 Properties and Behavior of Single Crystal Diamond in Fe Substrate Binder Wang Lan）Guo Ximian2) 1)Department of Material Science and Engineering,USTB,Beijing 100083,PRC 2)Department of Physics,USTB,Beijing 100083,PRC ABSTRACT When Single crystal diamond was set in Fe alloys and sintered on certain condition,it was found that the diamond was etched obviouly,but the crystal structure and strength was not changed;etching was occured on the interface between diamond and binder by the dissolving and diffusing of carbon atom in diamond crystal lattice into iron.Well controlled,Fe substrate binder diamond tool could obtain good properties. KEY WORDS etching,diffusion,diamondV O 1 . 1 8 N o . 5 王 岚等: 单 晶金 刚石在铁基合金 中的性态 与行 为 . 4 3 1 . 能的 损失 或 失效 . 因此 , 适 当控制 C 原子 的 扩散 和扩 散失 活 · , 才 能够 保证 F e 基 金 刚石工 具 的优 良性 能 . 4 结论 ( l ) eF 基 合金 对单晶金 刚石 的 中度刻 蚀 , 不 导致金 刚石 晶体的结 构转 变及 强度 变 化 . (2 ) eF 基 合金 (结 合剂 )对金 刚石 的刻蚀 在金 刚石 与结 合剂的界 面发 生 , 是金 刚石 晶格 中 的 C 原子 溶人 eF 并 在其 中扩 散 的过程 . ( 3) 适 当控 制 C 原子 扩 散和 C 原 子 的扩 散失 活 , 有 可 能获 得性 能 优 良的 eF 基 金 刚石 工 具 . 参 考 文 献 R a l e h e n k o P a t e m i n g V G , K o n o n e nk o T V . C a at lyt i e I n t e acr ti o n o f F e , N i a n d P t w i th D i a m o n d F i ln s : A PP li c a t i o n · 2 Jin S , G ar e b n e r J E . D i am o n d a n d R e lat e d M a t e ir a l s , 1 9 9 3 ( 2 ) : 9 0 4 ~ 9 0 9 M a s s i v e T h in i n g o f D i a m o n d F i ln s b y A D i fu s i o n Por e e s s . A PP I P h y s L e t , 1 9 9 2 , 6 0 ( 16 ) : 2 0 P r o P e rt i e s a n d B e h a v i o r o f S i n g l e C yr s t a l D i am o n d i n F e S u b s t r a t e B i n d e r l ) D e P a rt m e n t 2 ) 肠 n g 乙a n l ) G u o ix m ia n o f M a t e r i a l S e i e n e e a n d E n g i n e e r i n g , U S T B B e ij in g 10 0 0 8 3 , P R C D e P a rt m e n t o f P h y s i e s , U S T B , B e ij i n g 10 0 0 8 3 , P R C A B S T R A C T e o n d i t i o n . I t W h e n S i n g l e e ry s t a l d i a m o n d w a s fo u n d t h a t t h e d i a 们n o n d w a s s e t i n F e a ll o y s a n d w a s e t e h e d o b v i o u ly , b u t s i n t e r e d o n e e rt a i n th e c yr s ta l a fl d a n d l f o n . s t r e n g th w a s n o t c h a n g e d ; e t e h i n g w a s O C C u r e d e a r b o n o n ht C b e t w e e n S t f l C l l f e d i a m o n d b i n d e r b y t h e d i s s o l v i n g a n d d i肋 s i n g o f a t0 1】1 11 i l t e r af e e d i a m o n d c yr s t a l l a t i e e i n t o W e ll e o n t r o ll e d , F e s u b s tr a t e b i n d e r d i a m o n d t o o l e o u l d o b t a i n g o o d P r o P e rt i e s . K E Y W O R D S e t c h i n g , d i fu s i o n , d i a m o n d