D0I:10.13374/j.issn1001053x.1986.02.011 北京钢铁学院学报 1986年6月 Journal of Beijing University No.2 第2期 of Iron and Steel Technology June 1986 不锈钢亚型试样的氢致开裂和应力腐蚀 乔利杰褚武扬肖纪美 (金属物理教研室) 摘要 研究了奥氏体不锈钢Ⅲ型试样的氢致开裂和应力腐蚀。结果表明，动态充氢时Ⅲ型试样 也能发生氢致沸后断裂，且裂纹沿原缺口平面形核和扩展。从而可获得宏观平滑的扭转断口， 但断口上存在少量沿45”面的二次裂纹，一系列实验表明动态充氢能促进奥氏体不锈钢室温 蠕变，故在但扭矩下充氢能使扭转角不断增大，直至试样被断。奥氏体不锈钢Ⅲ型试样在 42%沸腾MgC1:溶液中也能发生应力腐蚀开裂，且裂纹在与缺口平面成45”的平面上形核和扩腰。 实验表明，无论是工型还是Ⅲ型，应力病蚀的门槛值均比氢致滞后断裂门槛值要低，例如 Ktscc/K:x=0.18,KIH/K1x-0.58,KEscc/Kx=0.13 KH/Kx-0.62. 关键词：应力腐蚀开裂 氢致开裂 奥氏体不锈钢 血型试样 Hydrogen Induced Cracking and Stress Corrosion Cracking of Austenitic Stainless Steel under Mode I Loading Qiao Lijie,Chu Wuyangy Xiao Jimei Abstract Hydrogen induced cracking(HIC of austenitic stainless steel under Mode III loading could occur during dynamic charging of hydrogen and the threshold stress intensity was K/K1x=0.62.The torsional angle, i.e.,the torsional plastic deformation,enlarged continuously during dynamic charging under a constant torque,which corresponded with increa- sing the external torque continuously,until the specimen was twisted to 1985-04-01收稿。 113年 月 第 期 北 京 钢 铁 学 院 学 报 。 ，口口 不锈钢 型试样的氢致开裂和应力腐蚀 乔利杰 褚武扬 肖纪美 金属物理教研室 摘 要 贾玲 研究 了奥氏体不锈钢 型试样的氢致开裂和应力腐蚀 结果表 明 ， 动态充氢时 型试样 也能发生氢致滞后断裂 ， 且裂纹沿原缺 口 平面形核和扩展 从而可获得宏观平滑的扭转断 口 ， 但断 口 上存在少量沿 ’ 面的二次裂纹 ， 一系列实验表 明动态充氢能促进奥氏体不诱钢室 温 蠕 变 ， 故在恒扭矩下充氢能使扭转角不断增大 ， 直至试样被扭断 。 奥氏体不锈钢皿型试样 在 妇多沸腾 ‘ 溶液中也能发生应力腐蚀开裂 ， 且裂纹在与缺口 平面成拈 的平面上形核和扩展 实验表明 ， 无论是 工型还是 型 ， 应力腐蚀的门槛值均比氢致滞后断裂门槛值要 低 ， 例 如 胶 一 一 台， ， ， 皿 。 皿 皿 “ ， 一 关锐词 应 力腐蚀开裂 氢致开裂 奥氏体不锈钢 址 型试样 曰网卿 ， ， 己 ，、 。 电卜 · · ， ， ， 一 ， 一 一 收稿 DOI ：10．13374／j ．issn1001－053x．1986．02．011