D0I:10.13374/j.issn1001-053x.1994.s1.018 第16卷增刊 北京科技大学学报 Vol.16 1994年3月 Journal of University of Science and Technology Beijing Mar.1994 S-TEN3和CRIA系列钢的耐硫酸 露点腐蚀性能 黄震中) 黄一忠D 付昌明) 李承秀) (1)北京科技大学表面科学与腐蚀工程系：2)上海第三钢铁厂) 摘要通过浸泡实验测出了S-TEN3、CRIA两类钢种在各种硫酸介质中的腐蚀速率。结果 表明，Sb和Ti分别能显著改善STEN3和CRIA钢的耐硫酸露点腐蚀性能。在此基础上，探讨 了合金元素在腐蚀过程中的作用。 关键词疏酸，露点腐蚀 Resisting Sulfuric Acid Dew Point Corrosion Property of Both S-TEN3 and CRIA H uang Zhenzhong H uang Yizkong Fu Changmin Li Chengrin) (i)Dept.of Surface Seience and Corrosion Engineering:2)The Third Iron and Steet Factory Shanghai ABSTRACT Corrosion rates of both S-TEN3 and CRIA steels are measured in various H2SO solutions by the immersed method.Based upon the experiments,the important role of alloy el- ements in corrosion course are discussed.The results show that Sb can obviously improve the resistance property of the S-TEN3 steel to sulfuritc acid dew point corrosion and so can Ti to the CRIA steel. KEY WORDS sulfuric acid,dew point corrosion 以重油为燃料的大功率发电锅炉以及工厂的各种锅炉燃烧废气中，一般都含有硫燃烧 而生成的S02和S03。常温下干燥的S0?对设备几乎不发生作用，但是烟气中一般含有水蒸 气(5%~18%)。当废气温度降低至露点以下或烟气接触到温度较低的烟道管壁或金属设 备时，废气中的SO,与冷凝水形成硫酸。即发生酸液的凝结并强烈地腐蚀金属。这种现象 被称为硫酸露点腐蚀。 小若正伦等人提出了钢的硫酸露点腐蚀“三段论”机制（如图1）。他们认为硫酸露 1993-09-20收稿第一作者男58岁副教授第 卷增刊 年 月 北 京 科 技 大 学 学 报 一 和 系列钢的耐硫酸 露点腐蚀性能 黄震 中 ‘ 黄一 忠 ‘ ， 付 昌明 ‘ ， 李承 秀 北 京科 技大学表面 科学 与腐蚀工 程 系 上 海第三钢铁 厂 摘 要 通过 浸 泡 实验 测 出 了 一 、 两类钢 种在各种硫酸介质 中的腐蚀速率 。 结果 表 明 ， 肋 和 分别能 显著改 善 一 和 钢的耐硫酸露点腐蚀性能 。 在此基础 上 ， 探讨 了合金元素在腐蚀过 程 中的作用 。 关键词 硫酸 ， 露 点腐蚀 一 夕 ， 之 夕 夕 夕 尸 ， 夕 乙 “ 无 夕 ‘ 一 一 · ， · 一 ’ ， 以重 油 为燃料 的大功率发 电锅 炉 以 及工 厂 的各种锅 炉燃烧废 气 中 ， 一般都含 有硫燃烧 而 生成 的 和 。 常温 下干燥 的 。 对 设 备几 乎不发 生作 用 ， 但是烟气 中一般含有水蒸 气 一 。 当废 气温 度 降低 至露 点 以 下 或烟气接 触到 温 度较 低 的烟道管壁或金属设 备 时 ， 废 气 中的 。 与冷凝 水形 成 硫酸 。 即发生 酸液 的凝结并强 烈地腐 蚀金属 。 这种现象 被称 为硫 酸露点腐蚀 。 小若正 伦川 等 人提 出 了钢 的硫酸 露 点腐蚀 “ 三段论 ” 机制 如 图 。 他 们认为硫酸露 一 一 收稿 第一 作者 男 岁 副教授 DOI ：10．13374／j ．issn1001－053x．1994．s1．018