D0I:10.13374/i.issn1001053x.1990.02.025 第12卷第2期 北京科技大学学报 Vo1.12No.2 1990年3月 Journal of University of Science and Technology Beijing March 1990 低合金钢一硝酸盐溶液体系的SCC图 吴荫顺· 摘要：研究了低合金钢硝酸盐溶液体系的应力府蚀行为。测定了温度、浓度和电极电 位对各种腐蚀类型及腐蚀强度的影响。进立了相应的温度~浓度-电位SCC阁。确定了该体系 的下临界电位和SCC敏感电位范围。讨论了采用阴极保护的可能性。 关键词：低合金钢，硝酸盐，应力腐蚀，下临界电位，SCC图 SCC Diagram for Low Alloy Steel-Nitrate Aqueous Solution System Vu Yinshun· ABSTRACT:The stress corrosion cracking (SCC)behaviour of low alloy steel in nitrate aqueous solution was investigated.The effect of temperature,medium concentration and potential on various corrosion types and thier intensities was determined.The temperature-concentration-potential SCC diagram was establi- shed.The down critical potential and sensibility zone of SCC was ascertained. The applicability of cathcdic protection was discussed. KEY WORDS:low alloy steel,nitrate,stresss corrsion cracking down critical potential,SCC diagram 硝酸盐水溶液可能在碳钢或低合金钢上引发应力腐蚀开裂(SCC)。常见的实例如以硝 酸盐为原料或产品的化工厂或化肥厂中的反应金【1)；硝酸盐肥料对地下管线的作用【2]，含 NOx冷凝液对治金厂高风温热风炉的腐蚀【3~J等。 一些研究者认为，燃料中的氮和空气中的氧与水分在热风炉高温下形成了Ox,继而生 成硝酸或硝酸盐，并冷凝在壳壁处。同时，燃烧脉动使壳板和钢管承受着脉动的拉伸应力， 并与热风炉加工应力、焊接残余应力一起和硝酸盐溶液的共同作用下，使壳板和钢管产生了 应力腐蚀开裂。 1990-04-12收稿 ·表面科学与腐蚀工程系(Dept,of Surface Sci.and Corro.Eng.) 131， 叫、 气 第 卷 第 期 北 京 科 技 大 学 学 报 年 月 低合金钢一硝酸盐溶液体系的 图 吴 荫 顺 ’ 摘 要 研究了 低合金钢 一 硝 酸 盐 溶 液体系的应 力腐蚀 行为 。 测定了温 度 、 浓 度和 电极电 位 对各种腐蚀 类型及腐蚀强度 的影响 。 建立 了 相应 的温 度 一 浓度 一 电位 图 。 确定了该体系 的下临 界电位 和 敏 感 电位 范 围 。 讨 论 了采 用 阴极保 护的可能性 。 关键词 低合金钢 ， 硝 酸盐 ， 应 力腐蚀 ， 下临 界电位 ， 图 一 平 ， 以 了 一 一 。 · ， ， ，。 从 一 ， 勺、 硝酸盐 水溶液可能在碳钢或低 合金 钢上弓发 应力 腐蚀 开裂 。 常见 的实例如 以 硝 酸盐 为原料或产品的化工厂或化 肥厂 中的反应 釜 ‘ 〕 硝酸 盐肥 料对 地下管线 的作 用 “ ’ 含 冷凝液对冶金厂高风温热 风 炉的腐蚀 “ 一 。 〕 等 。 一些 研究 者认为 ， 燃料 中的氮和空 气中的氧 与水分在 热风 炉高温下形成了 二 ， 继 而生 成硝酸 或硝酸 盐 ， 并冷凝在壳壁 处 。 同时 ， 燃烧脉 动使壳板和钢管承受 着脉 动的拉伸应 力 ， 并与热风 炉加工应力 、 焊接残 余应力一起和硝酸盐溶 液的 共 同作 用下 ， 使壳板和钢管产生了 应 力腐蚀开 裂 。 卜 一 一 收 稿 表面科 学与 腐蚀 工程 系 厂 飞 DOI ：10．13374／j ．issn1001－053x．1990．02．025