D0I:10.13374/j.issn1001053x.1986.s1.007 北京钢铁学院学报 1986年6月 Joarnal of Beijing University Special issue 专辑1 oi Iron and Steel Technology 61,1986,6 奥氏体型高温合金弯曲晶界普遍性的研究 葛占英于文秀杨莲隐孙庆标孙金贵叶锐曾 摘 要 对不同合金化程度的GH161,GH37,GH33镍基高温合金和GH36,GHG9铁基高温合金，采用固 溶后缓冷工艺或固溶后等温工艺处理，结果表明：均可形成弯曲晶界。同时发现形成弯晶的机制不仅与 热处理工艺有关，并与合金成份有关， 关键词：高温合金、弯曲品界.热处理。 Research of Zig-Zag Grain Boundary Universality in Austenitic Superalloys Ge Zhanying Yu Wenxin Yan Lianying Sun Qingbio Sun Jingui Yu Ruizeng Abstract Two kinds of heat-treatment m,thod are used for Ni-base superalloys 3 GH151,GH37,GH33,and Fe-base superalloys GH36 and GH69.The results show that the Zig-Zag grain boundaries are formed in ali these alloys.It has been found that the mechanism of Zig-Zag G.B.formation is dependent not only on heat-treatment method but on compositions of alloys. Key words,superalloys;zigzag grain boundary;heat treatment 前 言 高温合金使用温度较高，特别是在高温、长时应力作用下，蠕变断裂往往与晶界裂纹的 形成和发展有关。因此，晶界在高温状态下是一个薄弱环节，故强化晶界早已引起人们的广 泛重视。〔1一7) 改变晶界形状，使平直的晶界变为锯齿状或弯曲状，即“弯曲晶界”是强化晶界的重要 手段之一。由于弯曲晶界的存在，增大了晶界滑移阻力，提高了晶界裂纹萌生的临界切应力， 51匀 年 月 北 京 钢 铁 学 院 学 报 。 川 全 ， 专 辑 了 场 ， ， 之醉 沪 奥氏体型高温合金弯曲晶界普遍性的研究 葛 占英 于 文秀 杨莲隐 孙庆标 孙金贵 叶锐曾 摘 要 终邪 对不 同合金化 程 度的 场 ‘ ， 镍基 高温合金和 ， ” 铁基高 温合金 ， 采 用 固 溶后缓冷工艺 或 固溶后 等温工艺处理 ， 结果表呱 均 可形 成 弯曲晶界 。 同时发现形成弯 晶的 机制不仅 与 热处理 工艺 有关 ， 并 与合 金成份有关 。 关键词 高温合金 、 弯曲 晶界 、 热 处理 一 人 。 夕‘ 班 ￡ 。 夕￡ ” ’ 叼’ 犷 尸盯邵叼 》 一 一 ， ， ， 一 五 一 全 一 一 即 了 宜 前 言 诏制 翻 高温 合金使用温度较 高 ， 特别是在高温 、 长时应 力作用 下 ， 蠕变断裂往往 与 晶界裂纹 的 形成和 发展 有关 。 因此 ， 晶界在高温 状态下是一个 薄弱环 节 ， 故强化 晶界早 已引起人们 的广 泛重 视 。 〔 一 〕 改变晶界形 状 ， 使平直 的晶界 变为 锯齿状或 弯曲状 ， 即 “ 弯 曲晶界 ” 是强化 晶界的重要 手段之一 。 由于 弯曲晶界的存在 ， 增大 了晶界滑移阻力 ， 提高了晶界裂纹萌生的 临界 切应力 ， 里 DOI ：10．13374／j ．issn1001－053x．1986．s1．007