D0I:10.13374/j.issn1001-053x.1995.0M.011 第17卷第4期 北京科技大学学报 Vol.17 No.4 195年8月 Journal of University of Science and Technology Beijing Ag.1995 连俦热坯双频涡流探伤技术 李希胜 王绍纯 北京科技大学自动化信息工程学院，北京100083 摘要采用二维涡流探伤模型，研究了涡流传感器的结构参数对探伤灵敏度的影响，并将双频涡 流探伤技术用于坯料表面缺陷检测·结果表明，缺陷深度增加所引起的探头阻抗变化使其相角发 生变化· 关键词传感器，连铸坯，祸流检验，无损检验/无损探伤 中围分类号TG247 Research on Technique of Dual-Frequency Eddy-Current Inspection for Continuously Casting Hot Slab Li Xisheng Wang Shaochun College of Automation and Information Engineering,USTB,Beijing 100083,PRC ABSRACT Two-dimension eddy current inspection model is taken for researching the effect of the eddy current transducer structure parameter upon the inspection sensitivity.Dual-frequency eddy current inspection is applied to the inspection of slab surface defects.The results of experiment prove that the change of sensor impedance due to the change of crack depth causes the phase angle of impedance to change. KEY WORDS transducer,continuously casting slabs,eddy current test,non- destructive test non-destructive flaw detection 目前，国外进行连铸热坯探伤研究的方法主要有光学法和涡流法，光学探伤法可远离被 测热坯，免受高温辐射的影响，以增强系统可靠性·但对缺陷深度不能定量判别，使其应 用范围受到限制.涡流探伤法不仅能对缺陷深度作定量判别，还具有检测速度快，易自动化 等特点，比较适合连铸热坯表面探伤，本文选用涡流探伤法作为连铸热坯表面探伤方法· 1二维涡流探伤模型 实际的涡流探伤问题多为三维问题，为了简化分析，采用二维模型· 由洛仑兹互易定理可推出： △z=(1/可，(E×i-×)·nds (1) 1994-01-14收稿 第一作者男23岁硕士讲师第 卷 第 期 北 京 科 技 大 学 学 报 望巧 年 月 川 呢 卯 连铸热坯双频涡 流探伤技术 李希胜 王 绍 纯 北京科技大学 自动化信息工 程学 院 ， 北 京 幻 摘要 采用 二维涡流探伤模型 ， 研究 了 涡 流传感器 的结构参数对探伤灵敏 度的影 响 ， 并将双频涡 流探伤技术用于坯料表面缺陷检测 结果表 明 ， 缺陷深度增加所引起 的探 头阻抗 变化使其相 角发 生变化 关健词 传感器 ， 连铸坯 ， 涡 流检脸 ， 无损检验 无损探伤 中圈分类号 公打 一 一 戈 肠 叩 卿 户卫 以 泪 五而仙以 林邵 ， 几 ， 肠」毗 飞 一 期犯 ， 一 ， ， ， 一 一 目前 ， 国外 进行 连铸热坯 探 伤研究 的方 法 主要 有光学 法 和 涡 流法 光学 探 伤法 可远 离 被 测热坯 ， 免受 高温辐射 的影 响 ， 以 增 强 系 统 可靠性 但 对缺 陷深 度 不 能 定 量 判 别 ， 使其 应 用范 围受到 限制 涡 流探 伤法 不仅能 对缺 陷深度 作 定量 判别 ， 还具 有检测 速 度快 ， 易 自动化 等特点 ， 比较适合连铸热坯 表 面探伤 本文 选 用 涡流探 伤法 作为 连铸热坯 表面探伤方法 二维涡流探伤模型 实际的涡流探伤 问题多 为三 维 问题 ， 为 了简化分 析 ， 采 用 二 维模 型 由洛仑兹互 易定 理 可 推 出 △ 一 ， 凡 才 夕 ， 一 矛 穿 · 最 望科一 一 收稿 第一作者 男 岁 硕士 讲师 DOI ：10．13374／j ．issn1001－53x．1995．04．011