倪童伟等:高铌高磷GH4169C和GH4169合金的组织稳定性 ·1285· b 2 um (c) (d) m 图11两种合金在720℃时效不同时间组织形貌.(a)GH4169,30h:(b)GH4169C,30h:(c)GH4169,500h:(d)GH4169C,500h:(e) GH4169,1000h:(0GH4169C,1000h:(g)GH4169,10000h:(h)GH4169C,10000h Fig.11 Microstructures of the alloys after aging at 720C:(a)GH4169,30h:(b)GH4169C,30h:(e)GH4169,500h;(d)GH4169C,500h: (e)GH4169,1000h:(0GH4169C,1000h:(g)GH4169,10000h:(h)GH4169C,10000h (e)),至时效10000h,晶内y相含量大幅消减(图11 相,GH4169C合金中8相主要呈粗大的短棒状(图11 (g)和图12(c)).GH4169C合金8相同样粗化严重, (e)和11()),且没有魏氏体组织形成.GH4169C合 数量上也大幅增加.相比于GH4169合金中长针状8 金Y"相演变规律与GH4169合金一致,时效一开始就倪童伟等: 高铌高磷 GH4169C 和 GH4169 合金的组织稳定性 图 11 两种合金在 720 ℃时效不同时间组织形貌 . ( a) GH4169,30 h; ( b) GH4169C,30 h; ( c) GH4169,500 h; ( d) GH4169C,500 h; ( e) GH4169,1000 h; ( f) GH4169C,1000 h; ( g) GH4169,10000 h; ( h) GH4169C,10000 h Fig. 11 Microstructures of the alloys after aging at 720 ℃ : ( a) GH4169,30 h; ( b) GH4169C,30 h; ( c) GH4169,500 h; ( d) GH4169C,500 h; ( e) GH4169,1000 h; ( f) GH4169C,1000 h; ( g) GH4169,10000 h; ( h) GH4169C,10000 h ( e) ) ,至时效 10000 h,晶内 γ'相含量大幅消减( 图 11 ( g) 和图 12( c) ) . GH4169C 合金 δ 相同样粗化严重, 数量上也大幅增加. 相比于 GH4169 合金中长针状 δ 相,GH4169C 合金中 δ 相主要呈粗大的短棒状( 图 11 ( e) 和 11( f) ) ,且没有魏氏体组织形成. GH4169C 合 金 γ″相演变规律与 GH4169 合金一致,时效一开始就 ·1285·