D01:10.133741.is9m1001053x.2009.08.005 第31卷第8期 北京科技大学学报 Vol.31 No.8 2009年8月 Journal of University of Science and Technology Beijing Aug.2009 复吹转炉多功能法脱磷工艺 李建新)郝旭东12 仇圣桃)赵沛) 1)钢铁研究总院连铸技术国家工程研究中心，北京1000812)昆明理工大学材料与治金工程学院.昆明650093 摘要在不新增设备的前提下，通过优化转炉治炼工艺，使用复吹转炉多功能法进行铁水脱磷，提高转炉脱磷率。根据现有 转炉设备条件，通过热力学计算确定转炉前期脱磷温度范围，并在现场实验中掌握好倒渣时机、渣碱度、加料量和出钢温度， 确定最佳脱磷工艺.分析实验结果，与常规治炼相比，该脱磷工艺用原料量少，脱磷率稳定，且高达90%以上，在提高钢水质 量的同时也降低了生产成本. 关键词转炉；脱磷：出钢温度；热力学计算 分类号TF713.1 Dephosphorization technique of converters by multi-functional refining LI Jian-xin,HAO Xu-dong2).QIU Sheng-tao),ZHAO Pei) 1)Engineering and Research Center for Continuous Casting Technology.Central Ion and Steel Research Institute,Beijng 100081,China 2)Faculty of Materials and M ctallurgical Engineering.Kunming University of Science and Techndlogy.Kurming 650093,China ABSTRACT The dephosphorization rate of converters w as impo ved through optimizing the converter refining process and applying the method of multifunctional refining in converters on condition that any new equipment was not used.Based on the present com verter condition,the temperature range of dephosphorization was obtained by thermodynamics calculation.The suitable time of slag tapping.alkalinity of slag.tapping temperature and the quantity of material were determined,and finally the optimal dephospho- rization technique was confirmed.Comparing with normal refining,the quantity of material oould be reduced and the dephospho- rization rate was above 90%steadily by using the new technique.Besides,the quality of molten steel was impoved and the cost of production w as also decreased. KEY WORDS converter dephosphorization;tapping temperature;thermodynamic calculation 顶底复吹转炉自诞生以来至今，其治金功能日 围，以及前期脱磷和后期脱碳过程相关的工艺参数. 益得以完善，因为复吹转炉在铁水预处理过程中，可 宣化钢铁在转炉炼钢工艺上不断探索，针对转 提供优越的热力学和动力学条件，所以为铁水预处 炉治炼中终点磷偏高的问题，使用复吹转炉多功能 理脱磷创造了条件.顶底复吹转炉治炼技术是提高 法在不增加治炼设备的前提下，不仅使终点磷含量 产品质量、扩大品种、降低成本、减少喷溅和提高炼 降到001%以下，而且大大节省了原料量. 钢生产能力的重要手段之一， 转炉多功能法就是在铁水预处理过程中，利用 1实验条件与工艺 复吹转炉良好的热力学和动力学条件，进行前期脱 磷、倒渣，再进行后期脱碳，这样不仅在不增加治炼 1.1主要设备 设备的条件下，使转炉热效率大大提高，而且降低了 宣钢顶底复吹转炉的容量为110[，治炼时根据 铁水比，提高生产效率.本文根据热力学分析 治炼钢种入炉一定量的铁水，另兑入部分废钢.废钢 结合现场实验，确定了复吹转炉脱磷期控制温度范 比约在10%左右. 收稿日期：200811-18 基金项目：国家科技支撑计划资助项目(No.20O6BAE03A00) 作者简介：李建新(1963一），男，教授级高级工程师，博士.E-maik xuangangl@126.mm复吹转炉多功能法脱磷工艺 李建新1) 郝旭东1, 2) 仇圣桃1) 赵 沛1) 1) 钢铁研究总院连铸技术国家工程研究中心, 北京 100081 2) 昆明理工大学材料与冶金工程学院, 昆明 650093 摘 要 在不新增设备的前提下, 通过优化转炉冶炼工艺, 使用复吹转炉多功能法进行铁水脱磷, 提高转炉脱磷率.根据现有 转炉设备条件, 通过热力学计算确定转炉前期脱磷温度范围, 并在现场实验中掌握好倒渣时机、渣碱度、加料量和出钢温度, 确定最佳脱磷工艺.分析实验结果, 与常规冶炼相比, 该脱磷工艺用原料量少, 脱磷率稳定, 且高达 90%以上, 在提高钢水质 量的同时也降低了生产成本. 关键词 转炉;脱磷;出钢温度;热力学计算 分类号 TF713.1 Dephosphorization technique of converters by multi-functional refining LI Jian-xin 1) , HAO X u-dong 1, 2) , QIU Sheng-tao 1) , ZHAO Pei 1) 1) Engineering and Research Center for C ontinuous Casting Technology, Central Iron and S teel Research Institut e, Beijing 100081, China 2) Faculty of Mat erials and M etallurgical Engineering, Kunming University of Science and Technology, Kunming 650093, China ABSTRACT The dephosphorization rate of converters w as impro ved through optimizing the converter refining process and applying the method of multi-functio nal refining in converters on condition that any new equipment was not used.Based on the present co n￾verter condition, the temperature range of dephosphorization w as obtained by thermodynamics calculation.The suitable time of slag tapping, alkalinity of slag, tapping temperature and the quantity of material were determined, and finally the o ptimal dephospho￾rization technique w as confirmed .Comparing w ith normal refining, the quantity of material could be reduced and the dephospho￾rization rate w as above 90 % steadily by using the new technique.Besides, the quality of molten steel w as impro ved and the cost of production w as also decreased. KEY WORDS converter;dephosphorization ;tapping temperature;thermodynamic calculation 收稿日期:2008-11-18 基金项目:国家科技支撑计划资助项目( No .2006BAE03A00) 作者简介:李建新( 1963—) , 男, 教授级高级工程师, 博士, E-mail:xuangangljx @126.com 顶底复吹转炉自诞生以来至今, 其冶金功能日 益得以完善, 因为复吹转炉在铁水预处理过程中, 可 提供优越的热力学和动力学条件, 所以为铁水预处 理脱磷创造了条件.顶底复吹转炉冶炼技术是提高 产品质量 、扩大品种、降低成本 、减少喷溅和提高炼 钢生产能力的重要手段之一[ 1] . 转炉多功能法就是在铁水预处理过程中, 利用 复吹转炉良好的热力学和动力学条件, 进行前期脱 磷、倒渣, 再进行后期脱碳, 这样不仅在不增加冶炼 设备的条件下, 使转炉热效率大大提高, 而且降低了 铁水比, 提高生产效率[ 2-4] .本文根据热力学分析 结合现场实验, 确定了复吹转炉脱磷期控制温度范 围, 以及前期脱磷和后期脱碳过程相关的工艺参数. 宣化钢铁在转炉炼钢工艺上不断探索, 针对转 炉冶炼中终点磷偏高的问题, 使用复吹转炉多功能 法在不增加冶炼设备的前提下, 不仅使终点磷含量 降到 0.01 %以下, 而且大大节省了原料量. 1 实验条件与工艺 1.1 主要设备 宣钢顶底复吹转炉的容量为 110 t, 冶炼时根据 冶炼钢种入炉一定量的铁水, 另兑入部分废钢, 废钢 比约在 10 %左右. 第 31 卷 第 8 期 2009 年 8 月 北 京 科 技 大 学 学 报 Journal of University of Science and Technology Beijing Vol .31 No.8 Aug.2009 DOI :10.13374/j .issn1001 -053x.2009.08.005