D0I:10.13374/i.is8n1001053x.1991.03.029 北京科技大学学报 第13卷第3期 Vol.13 No.3 1991年5月 Journal of University of Science and Technology Beijing May 1991 沥青碳纤维导电行为及其应用 范晓波·姜荣跃·余宗森· 摘要：对通用型莎青基预氧化纤维在碳化过程中的电阻变化行为进行了测试。结果表 明：碳化过程中纤维的电阻率可由10122-cm下降到10-1？-cm,得到了纤维电阻率与碳化 温度之闻的定量关系：并通过纤维电阻事的变化与纤维元素分析结果之间的对应关系，表明 纤维在碳化过程中发生结构转变。给出了利用碳纤维导电性的应用实例。 关键词：沥青基碳纤维，电阻事，碳化 Electric Resistance Behavior of Pitch-Base Carbon Fibers and Its Application Fan Xiaobo·Jiang Rongyao·Y4 Zongson" ABSTRACT:The electric resistance behavior of pitch-base preoxidized fibers during the carbonization is measured.The conclusions have shown that the fiber's resistivities during the carbonization decrease from 1012Q-cm to 10-1 Q-cm.And the quantitative relation between the fiber's resistivities and the carbonized temperatures is got.Using the relation of fiber's resistivities and the results of fiber's element analysis infers the constructive changes of the fiber during the carbonization.The example of the carbon fiber's electric co- nductivity used has been given. KEY WORDS:pitch-base carbon fiber,electric resistivity,carbonization 1990-09-27收稿 ·材料物理系(Department of Materials Physics) 262第 卷第 期 年 月 北 京 科 技 大 学 学 报 。 沥青碳纤维导电行为及其应用 范晓渡 ’ 姜荣跃 ’ 余宗森 ’ 摘 要 对通用型沥青基顶氧化纤维在碳化过程 中的 电阻变化行为 进行 了 测试 。 结果表 明 碳化过程中纤维的电阻率可 由 口 一 下降到 。 · 口 一 ，得 到 了纤维 电阻率与碳化 温度之 间的定量关 系， 并通过 纤维 电阻率的变化与纤维元素分析结果之 向的对应关 系 ，表 明 纤 维 在碳化过 程中发 生结构转变 。 给 出了利用碳 纤维导 电性的应用实例 。 关镇词 沥青基碳纤维 ， 电阻率 ， 碳化 一 ” 石。 ‘ ’ 儿 ’ 括 ’ 一 。 ’ 一 一 。 五 ’ 。 ’ ’ 一 ’ 。 一 ， 丁， 一 一 收稿 材料物理 系 DOI ：10．13374／j ．issn1001－053x．1991．03．029