Abstract The present work has found that the transverse rupture strength of WC-Co hard metals can be improved by quenching heat treatment. The icrement of transverse rupture strength(TRS)is dependent on the cobalt content of hard metal.The higher the cobalt content of hard.metal is,the more the increament of transverse rupture strength is,The main rea son is that the transformtion of face centered cubic cobalt stable at high temperature to hexagonal closepacked can be depressed by quenchin g heat treatment.The transformation temperature increases with the increa- se of cobalt content of hard metal by means of differential thermal anaysis because binder phase of high cobalt hard metal contains higher tungsten content than that of low hard metal during reheating, Key words:cobalt binder phase,transformation temperature,hard metal 前 言 WC-Co系硬质合金通过谇火热处理来提高其力学性能近年来已引起了人们的注 意〔1,2)，淬火热处理之所以能提高硬质合金的力学性能，其主要原因是由于淬火可将高 温下稳定面心立方钴粘结相全部或更多的保留到室温。为了合理地选择WC-C0硬质合 金的谇火温度，就需要了解加热过程中钴粘结相由密排六方结构转变成面心立方结构的 温度。本研究用差热分析仪对4种不同钴含量的硬质合金的粘结相的相变点进行了测 定，并对其转变点的差异进行了分析讨论。此外还对WC-Co硬质合金热处理后的性能 及其微观组织结构进行了分析研究。 1 实验方法 1.1实验方案 (1)为了能给WC-8%Co(YG8),WC-10%Co-5%TaC(YG105),WC- 15%Co(YG15),WC-20%Co(YG20)硬质合金淬火处理提供较准确的淬火温度， 对以上4种成分的硬质合金的钴粘结相由密排六方(hcp)转变成面心立方(fcc)的 相变点温度用差热分析仪进行了测定。 (2)分别对以上3种WC-Co硬质合金进行淬火热处理，并对WC-8%Co合金 进行回火处理，研究热处理对合金性能的影响，并对硬质合金热处理后的组织结构进行 了研究。 184一 皿 ， ， ， ， 一 前 言 一 系 硬 质合金 通 过淬火 热处理来提高 其力 学性能近 年来已 引起 了 人 们 的 注 意 〔 ， “ 〕 ， 淬 火 热处理之所 以能提高硬质合金 的力 学性能 ， 其主要原 因是 由于淬火可将高 温下稳 定面心 立方钻粘结相 全部或 更多的保留到 室 温 。 为 了合理地选择 一 。 硬质 合 金 的淬 火温度 ， 就需要 了解 加 热过程 中钻 粘结相 由密排六方结构 转变成面心立方 结 构的 温度 。 本研究用差热分析仪对 种 不 同钻 含量的 硬 质合金 的 粘结相 的相 变 点进 行 了 测 定 ， 并对其转变点的差异进行 了分析讨论 。 此外还对 一 。 硬 质合金 热处理后的性 能 及其微观组织 结构进行 了分析研究 。 实验方法 实验方 案 为 了能给 一 ， 一 一 ， ， 一 。 硬质合金淬火处理提 供 较准确 的淬火温 度 ， 对 以上 种 成 分 的硬质合金 的钻 粘结相 由密排六方 转变成 面心 立 方 的 相 变 点温 度用 差 热分析仪进行 了测 定 。 分别 对 以上 种 一 。 硬质合金进行淬火 热处理 ， 并 对 一 。 合 金 进 行 回火处理 ， 研究 热处理对合 金性 能的影响 ， 并对硬质合金 热处理后的组织结构进行 了研究