Table 2 Contents cf some elements in steel No. Added Content of elements in steel,wt Yttrium heat % P S Al 0 Y 1 0 0.010 0.020 0.038 0.0096 0 2 0.091 0.010 0.021 0.170 0.0082 0.014 9 0.277 0.010 0.015 0.220 0.0078 0.053 4 0.553 0.010 0.010 0.390 0.0044 0.190 The experiments show that the yield of yttrium is dependent on its initial concentration.Yield of yttrium is increased with the added amouot of modifi- cator as follows:15.4%6-for heat No.2;19.1%-for No.3 and 34.4%-for No.4.The relationship between contents of S and O in steel and residual concen- tration of Y was shown in Fig.2. The results of the research shows,a small amount of yttrium in steel has not observable influence on the variation of sulfur in steel.This is in agreement with result of reference [4. 2.2 Thermodynamic Calculation of Decxidation with Vttrium Reaction betwcen yttrium and oxygen may be【s】 mCY]+ncO]=YmO(s) Further more in our condition it may be 2CY)+3[0]=Y2O3(s) K=aa=(fC%Y])(fo%)) In case of minimum in the relationship of [and [%Y],then d〔%O) d〔%Y) =0 893>0 From first expressicn we can get 2.303c%Y)-(e+ne From second expression we shall have 2.303〔%0>〔-加0-ne8 The interaction coefficents are taken from reference [4,5) e8=-0.20;e￥=0.006：e=-16.3;e9=-01.58 Inserting them in the expressions and the results can be cbtained by solution 541七 。 ， 从 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 。 ， · 手 · 二 百 一 。 · 。 一 一 石 一 · · 飞 认 · 认 一 ， · 、 、 ， · 二 · 〔 〕 。 。 卜 己 ， 已 。 。 士卜 毖 士 〕 ， ，长 〔 〕 〔 〕 〔 〕 〔 〕 。 和 君 八 〔 〕 几 。 〔 〕 ” 〔 〕 〔 〕 ， 〔 〕 〔 〕 〔 〕 〔乡石 〕 权 泞艺 。 · 〔 〕 〕 勺口 心‘ · 魂八少 珍 下 广七 一 。 义 ， 从 · 五 、 一 聋 一一 二 〔 一 ， 艺 。 为 加 时 一 。 北〕 ， 。 落 女 〔 ， 〕 仑 一 时 八曰 。 此 一 亡 一一 。 一 〕 。 卜