D0I:10.13374/i.issn1001-053x.1990.02.026 北京科技大学学报 第12卷第2期 Vo1.12No.2 1990年3月 Journal of University of Science and Technology Beijing March 1990 Fe25Cr20Ni2,4Si合金在H2S-H2中 的高温疏化行为 周春根黄震中朱日彰 滴要：本文使用连线称重装置和非连绕称重装置对Fc25Cr20Ni2.Si合金在 H2S-H2气氛中的高温疏化行为进行了研究。结果表明：这种合金的硫化动力学行为遵循 抛物线规律。腐蚀产物有三层：最外层（称OL-I层）由F©-Ni-S系统组成，中间层（称 OL-I层)由Fc-Cr-S系统组成，内硫化层(Subscale)由一些弥散的硫化物相组成。 标记实验的结果表明：合金在疏化过程中，腐蚀产物的最外两层的生长是由金属离子向外扩 散控制，而内硫化层的生长是由分解机理控制。 关键词：动力学，硫化，腐蚀，扩散 Sulfidation Kinetics of Fe25Cr20Ni2,4Si in H2S-H2 Atmosphere Zhou Chungen Huang Zhenzhong Zhu Rizhang'. ABSTRACT:The sulfidation kinetics of Fe25Cr20Ni2.4Si were carried out at H2S-H:atmospheres by means of continuously-weighing device and non-conti- nuously weighing device.Sulfidation kinetics curves of the alloy obeys parabolic law.The composition and morphology of sulfide scales were also studied.All sulfide scales consist of two surface layers in addition to subscale.Two surface layers are controlled by predominante diffusion of metals.The subscale grow is controlled by the inward diffusion of sulfur. KEY WORDS:kinetics sulfidation,corrosion,H2S,diffusion 在煤的转化、石油化工等企业中存在着严重的高温硫腐蚀，因此研究高温硫化具有很重 要的意义。目前，对Fe25Cr20Ni2.4Si合金的硫化行为的研究未见报道，本文对这种合金的 硫化行为进行了较为详细的研究。 1989-04-12收稿 ·表面科学与脑蚀工程系(Dcpt,of Surface Sci,and Corro,Bng,) 137权 第 卷 第 期 年 月 北 京 科 技 大 学 学 报 。 、 。 名 合金在 一 中 气 、 的高温硫化行为 周春根 黄震 中 朱 日彰 ’ 摘 要 本 文 使 用 连 续 称 重 装 置 和 非 连 续 称 重 装 置 对 合 金 在 一 气氛中的 高温 硫化 行 为进 行 了研究 。 结果 表明 这 种 合金 的硫化 动力学 行 为 遵循 抛 物线规 律 。 腐蚀 产物 有三层 最外层 称 一 层 由 卜 卜 系统组成 ， 中间层 称 一 工层 由 一 一 系统组成 ， 内 硫 化 层 由一 些 弥 散 的硫化 物相组 成 。 标 记 实验 的结果表明 合金 在 硫化过程 中 ， 腐蚀 产物 的最外 两层 的生 长是 由金属 离子 向外扩 散 控 制 ， 而 内硫化 层的生 长 是 由分 解机理控 制 。 关 键词 动力学 ， 硫化 ， 腐蚀 ， 扩散 。 一 赵 万 二 夕 “ 之 ’ 一 一 一 一 住 一 一 · ， ， 声 ， 在煤 的转化 、 石 油化工等企业 中存在着严重 的 高温 硫 腐蚀 ， 因此研究高温硫 化具有很重 要的意义 。 目前 ， 对 合金 的硫化行为 的研 究未见报道 ， 本文 对这 种合金 的 硫化行为进 行了较为详细 的研究 ， 一 一 收稿 表面 科学 与腐蚀工程系 DOI ：10．13374／j ．issn1001－053x．1990．02．026