D0I:10.13374/i.issn1001-053x.1990.02.019 北京科技大学学报 第12卷第2期 Vo1.12No.2 1990年3月 Journal of University of Science and Technology Beijing March 1990 非晶态Ni-P合金在碱性介质中 的阳极行为 孙冬柏 朱应扬杨德钩张文奇· 摘要：用动电位极化方法研究了3种不同化学饿工艺得到的N-P非品态合金镀层，在 1mo1/1NaOH碱性介质中的阳极极化行为，并通过XPS分析了不同极化电位下的表面膜。 结果表明：在所研究的体系中不存在随P增加阳极溶解电泷下降的规律，尽管合金表面存在 H2PO三和PO4离子，但并没有有效地抑制Ni-P合金的阳极溶解。P的强烈的水化作用可能 是导致非品态Ni-P合金的阳极溶解电泷比纯Ni更大的主要原因。 关键词：非晶态，阳极溶解，NP合金，化学陵 Polarization Behaviour of Amorphous Ni-P Alloys in NaOH Solution Sun Dongbai Zhu Yingyang Yang Dejun Zhang Wengit ABSTRACT:Polarization behaviour of electroless amorphous Ni-P alloy coatings have been investigated in 1mol/l NaOH solution using potentiodynamic method,and surface films at different potentials have been analysed on the basis of XPS method.Results indicate:the anodic dissolution current does not decrease with the increase of P content in the Ni-P alloy,even though there exists H2PO2 and PO on the surface film,anodic dissolution of alloys has not been inhibited effectively.The intense hydrolization of P may be the cause of making the dissolution current of Ni-P alloy higher than that of Ni. KEY WORDS:amorphous,anodic dissolution,Ni-P alloy,chemical coating 有关化学镀非晶态Ni-P合金镀层的耐蚀性的评价和钝化机理至今仍没有统一观点。 J.FIis和D.J,Duyuettet1J认为：P使Ni在碱性和中性介质中的阳极溶解活性增大：P的 1989-04-12收稿 ·8级华业生马若刚参加了实验工作 ··表面科学与腐蚀工程系(Dcpt.of Surface Sci.and Corro,Eng) 97、 、 第 卷第 期 年 月 北 京 科 技 大 学 学 报 非 晶态 一 合金在碱性介质 中 的阳极行为 气 、 孙冬柏 朱应扬 杨德钧 张文奇 摘 要 用动电位 极化 方法研究了 种不 同化 学镀工艺得 到 的 一 非晶态合金镀 层 ， 在 碱性介质中的阳极极化 行为 ， 并通过 分析了不同极化 电位下的表面膜 。 结果表明 在所 研究 的体系中不 存在随 增加 阳极溶解电流下 降的规 律， 尽管合金表面存在 百和 万离子 ， 但并没有有效 地抑 制 卜 合金 的阳极溶解 。 的强 烈 的水化作 用可能 是导致非晶态 卜 合金的 阳极溶解电流 比纯 更大 的 主要原 因 。 关健词 非 晶态 ， 阳极 溶 解 ， 卜 合金 ， 化学 镀 、 、 一 ‘ 路 ” 夕 “ 夕夕 夕 昨夕 牙 、 、 一 ， 一 ， 万 牙 ， 扭 一 ， 、 ， 一 ， 有关化学 镀非 晶态 一 合金 镀层 的耐蚀性 的评价和钝化机理至今 仍 没 有 统一观 点 。 和 。 二 〔 ’ 〕认为 使 在碱性和 中性介质 中的阳极溶解活性增 大 的 吕 一 一 收稿 ‘ 、 份 级毕业生马若刚参加了实 验工作 表面科学 与腐蚀工程系 DOI ：10．13374／j ．issn1001－053x．1990．02．019