grow just adjacent to iron matrix.For the scales of carbon steel the iron matrix was not protected fron atmospheric corrosion for iron hydroxide was made as "harbour"between scale and metal,Magnetites and hematites were formed on the surface of hot-rolled plates,The scale with developed magnetite and a sawtooth structure connected with matrix coule provide a good protection to the matrix. The rare earth added made the.steel clearer and inclusions more g ranular.It seems that rare earth in the steel inhibited the decomposi- tion of magnetite under the reaction with water and air.The steel treated by rare earth had better atmospheric corrosion resistance. Key wards:corrosion-resistance steel,scale,the composition of minerals,microstructure 前 言 为衡量铁路用耐大气腐蚀钢的耐蚀性，除了用电化学测试法、氧化增重、失重等方 法外，我们还用矿相学研究方法(1)，研究耐蚀钢及与之作比较的一些普通钢种的氧化皮 物相组成、显微结构与耐蚀性的关系。 1 实验条件 研究试样共途用7种国产和进口的冷轧及热轧钢板，其成分见表1。将各种钢的板 状试样置于雾化箱中处理56天（每隔0.5h,喷蒸馏水0.5h,相对湿度95%)，取出后 进行研究。 表1 试验钢的化学分析 Table 1 Chemical analysis of steels Rolling No. Steel Chemical composition, C Si Mn P RE Cu Cr Ni Cold.rolled 】 A3 0.210.270.550.010.009 - plares 2 C0r-ten40.0720.410.370.1090.031 0.310.8650.38 3 Imported0.0960.350.40 0.100.008 0.28 0.390.225 cor-tenA Hot-rolled A3 0.21 0.270.570.100.009 plaies 5 08PV 0.100.220.520.1230.0290.11- 08PVRE0.090.220.550.1010.0300.070.055 7 08 CuPVRE0.010.320.600.1050.0070.060.0090.28 2“ ， ’ 一 尹 · 叮 、 ‘ ’ 一 ， ， ， 前 言 为衡量铁 路用 耐大气腐蚀钢的耐蚀 性 ， 除 了用 电化学测试法 、 氧 化增重 、 失重 等方 法外 ， 我们还用 矿相学研究 方法〔 ” ， 物相组成 、 显微结构与耐蚀 性的关 系 研究耐蚀钢及与之 作比较的一些普通钢种的氧化皮 实验条件 研究试 样共选 用 种 国产 和进 口 的冷轧 及热轧钢板 ， 其成分 见表 。 将各种钢 的板 状试样置于雾 化箱 中处理 天 每 隔 ， 喷蒸馏水 ， 相对 湿度 ， 取 出 后 进行 研究 。 坟 表 试 验 铜 的 化 学 分 析 丽 川 ， ， 绍 一毛 一 一 一 人 亡 一 人 。 ， 。 。 ， 。 。 。 一 。 。 。 。 ， 一 。 一