D0I:10.13374/j.issnl001-053x.1987.s2.024 北京钢铁学院学报 1987年2月 Journal of Beijing University Specjal issue 专辑1 of Iron and Steel Technology No.1,1987.2 应力腐蚀裂缝内电化学行为的研究进 展情况和存在的问题 李德林‘朱日彰 张文奇 (表面科学与腐蚀工程系) 摘要 应力膏做裂连内电化学行为的研究方法分为实际测魔、模拟刚试和理论计算三种。本文简珞地介绍和评述了各 种研究方法的进腰情况及优缺点。存在的主要问赐是：裂尖的电化学动力学过程、裂缝内电谦及阻抗的分布规律、 外部极化对裂尖电化学状态的影响等尚不清楚。 关健词：应力腐蚀、电化学、裂尖 Progresses and Problems in the Research of Electrochemical Behaviors Within Stress Corrosion Cracks Li Delin Zhu Rizhang Zhang Wengi Abstract The methods for the research on the electrochemical behaviors within stress corrosion cracks are reviewed,which consisted of pratical and modeled measurements and theoretical alalysis.Three important but unclear problems are alse prosented,these are processes of electrochemical kinetics at cracktips,the distributions of current and inpedence within cracks and the influence of polarization on the olectrochemistry of crack tips. Key words stress corrosion crack:electrochemical;crack tip 前 应力腐蚀断裂是最严重的局部腐蚀之一，它的关键部位是处于三轴向受力状态的闭 88北 京 钢 铁 学 院 学 报 生吕 年 今 专 辑 。 ， 。 应力腐蚀裂缝内电化学行为的研究进 展情况和存在的 问题 李德林 ’ 朱 日彰 张 文奇 表面科学与启蚀工 程 系 摘 要 应 力房蚀裂缝内 电化 学行为的研究方 法分为 卖际测盆 、 模拟 测 试和理 论计算三 种 。 本文简略地介绍 和 评述 了各 种 研究方 法的进展情况 及优 缺点 。 存在 的 主 要问肠是 裂 尖的电 化学 功力学过程 、 裂 缝 内电流及阻 抗的分布规津 、 外 部 极化对裂尖电化学状 态的影响等尚不 清楚 。 关健 词 应 力嘴蚀 、 电化学 、 裂 尖 己 ” 渭 扮 九 廿 叮 比 五 。 ， 心 三‘ 竹 班 几 ， 。 洛 ， 弓 沪 七 小 哟 山 韶 ， 前 言 应力腐蚀断裂是最严重的局部腐蚀之一 ， 它的关键部位是处于三轴 向受力状 态的闭 DOI ：10．13374／j ．issn1001－053x．1987．s2．024