D0I:10.13374/i.issn1001-053x.1989.01.012 第11卷第1期 北京科技大学学报 Vol.11No.1 1989年1月 Journal of University of Science and Technology Beijing Jan 1989 α'相形成与铁铬铝合金的脆性 杜国维蔡家敏 章小雁 (北京料技大学) (北京钢丝厂) 摘要：应用电子显微镜、X射线衍射技术，对低温长期使用的铁铬铝电热合金进 行分析。结果表明：品粒长大以及铬原予含量为75%左右的铁铬二元：/相在晶界和基体中析 出，是导致合金变跪的主要原因；通常微量碳化物C「23Cg相以及·相总是沿晶界分布。 关键词：铁铬铝合金，电热合金，品粒平均直径，断裂 a Phase Formation and Embrittlement of Fe-Cr-Al Alloy Du Guowei Cai Jiamin Zhang Xiaoyan ABSTRCTA:Using electron microscopy and X-ray diffraction techniques, the structure changes of Fe-Cr-Al alloy being used at low temperature for a long time were investigated.The results demonstrated that increase in embri- ttlement for the alloy was mainly caused by grain growth and a'-phase preci- pitation which contained 75 at%Cr;as usual,small amount o-phase and carbide Cr2sCe precipitated at grain boundaries. KEY WORDS:Fe-Cr-Al alloy,electro-heating alloy,embrittlement,fracture, grain average diameter 体心立方结构的铁铬铝合金，作为电热元件，在使用过程中很快变脆，在热应力或其它 外力作用下，导致合金断裂]。在高温下合金晶粒极易长大，当品粒平均直径大于100μm 时，合金呈现穿晶解理断裂。本文试图分析合金在低温下使用条件，来自合金内部变化，指 出导致合金变脆原因，为发展与提高合金质量提供依据。 1986一04一25收稿 63第 卷第 期 。 年 月 北 京 科 两 、 技 大 学 学 报 对。 。 。 ’ 相形成与铁铬铝合金的脆性 杜 国维 蔡家敏 北 京科 技 大学 章小 雁 北京钢丝 厂 、 摘 要 应 用 电子显微铰 、 射 线衍射技 术 ， 对低温长期使 用 的铁铬 铝 电热 合 金 进 行分 析 。 结果表 明 晶粒长大 以 及铭原 子 含量为 左 右 的铁铬二 元 。 ，相 在 晶界 和 基 体 中析 出 ， 是导 致 合金变脆 的主 要原 因 通常 微量碳化 物 。 相 以及 二 相总是沿 晶 界分 布 。 关趁 词 铁铬 铝 合金 ， 电热 合金 ， 晶粒平 均 直径 ， 断 裂 ’ 一 一 、 、 ， “ 田 川 口 一 手 厂 ， 一 一 · 川 ’ 一 “ ， 一 匆‘ 川 一 一 人 。 ， 一 ， ， ， 体心立方结 构的铁铬铝 合金 ， 作为 电热 元件 ， 在 使用过程 中很 快变脆 ， 在热应力或其它 外 力作用下 ， 导致 合金 断 裂 川 。 在 高温下合金 晶粒极 易长大 ， 当晶粒平均直径大 于 。 拌。 时 ， 合金呈 现穿 晶解 理断 裂 。 本文试 图分析 合金 在低 温下 使用 条件 ， 来 自合金内部 变化 ， 指 出导致合金 变脆原因 ， 为发 展与 提高合金 质量提供依 据 。 一 一 收稿 DOI ：10．13374／j ．issn1001－053x．1989．01．012