D0I:10.13374/i.is8n1001053x.1993.01.022 第15卷第1期 北京科技大学学报 Vol.15 No.1 1993年1月 Journal of University of Science and Technology Beijing Jn.1993 长城1号防护涂层抗热腐蚀的性能 叶锐曾*孙金贵· 廖小宁 吕反修·于文秀· 摘要：用等离子喷涂方法将长城】号及X-40涂层镀复在GH864高温合金试样上，然后进行 热腐蚀试验，并用OM、SEM、EMPA进行性能分析。结果表明，长城1号涂层显示出比 X-40涂层更优越的腐蚀抗力。提出了长城1号、X-40涂层及GH864基体合金可能的腐蚀机 制。 关键词：热商蚀，涂层，等离子喷涂 Investigation of Hot Corrosion of Great Wall No.1 Coating Ye Ruizeng'Sun Jingui'Liao Xiaoning Lu Fanxiu'Yu Wenxiu ABSTRACT:High temperture corrosion tests in 75%NaSO-25%NaCi molten salt have been conducted on GH864 superalloy specimens plasma sprayed with great wall No.I and X-40 coatings.After the corrosion tests.each sample was examined by OM,SEMand EMPA.It was found that X-40 coating was severely corroded by the molten salt due to cracking and spalling,whereas the Great Wall No.I exhibited superior corrosion resistance. KEY WORDS:hot corrosion,coating,plasma spraying 烟气轮机实际运行中遇到的是冲蚀-低温热蚀交互作用问题：。叶片在烟气流中受 到氧化与腐蚀，形成较疏松的腐蚀产物，它很容易披催化剂硬质粒子冲蚀掉，如此循环往 复直至叶片完全失效。因此，烟机叶片防护涂层的成分设计必需同时考虑冲蚀与低温热蚀 这两个重要因素及其交互作用。 本文重点研究长城【号（用C-1代表)新型防护涂层的抗热腐蚀性能，作为比较也 引入了X-40等其它涂层的有关性能。 1 实验方法 1992-06-17收稿 ◆材料科学与工程系(Department of Materials Science and Engineering) 第一作者叶锐曾男62教授第 巧 卷 第 I 期 19 9 3 年 l 月 北 京 科 技 大 学 学 报 J o u rn a l o r U n i v e rs i ty o f s c i e n e e , n d T e e h n o l o g y B e i弃n g V 0 1 . 15 N o . l J a n . I 99 3 长城 1 号防 护涂层抗热腐蚀 的 性能 叶锐 曾 * 孙 金 贵 ’ 廖 小宁 ’ 吕反 修 ` 于文 秀 ’ 摘 要 : 用等 离子喷 涂方法 将长 城 l 号 及 X 一 40 涂层镇 复在 G H 8 64 高温 合金 试样 上 , 然后 进行 热 腐 蚀试 验 , 并 用 O M 、 S EM 、 E M P A 进 行性 能 分析 。 结 果 表 明 , 长 城 1 号涂 层显 示 出 比 X 一 4 0 涂层更 优越 的腐蚀抗 力 。 提 出 了长城 1 号 、 X 一 4 0 涂层 及 G H 86 4 墓 体合金可能的腐蚀机 制 。 关键词 : 热腐蚀 , 涂层 , 等离 子喷涂 1 n v e s t l g a t i o n o f H o t C o r r o s i o n o f G r e a t w a l l N o . I C o a t i n g eY R u i : e n g ` S u n l’nJ g u i . L .aI o X ia o n in g . L u F a n x i u . Y “ 分e n x i “ . A B S T R A C T : H i g h t e m P e r t u r e e o r r o s i o n t e s t s i n 7 5 % N a Z S O ` 一 2 5% N a C I m o lt e n s a lt h a v e b e e n e o n d u e t e d o n G H 8 6 4 s u P e r a ll o y s p e c im e n s p l a s m a s P r a y e d w i t h g r e a t w a ll N o . l a n d X 一 4 0 e o a t i n g s . A ft e r t h e e o r r o s i o n t e s t s , e a c h s a m p l e w a s e x a m i n e d b y O M , S E M a n d E M P A . I t w a s 阳u n d t h a t X 一 4 0 e o a t i n g w a s s e v e r e l y e o r r o d e d b y t h e m o lt e n s a lt d u e t o e r a e k i n g a n d s P a lli n g , w h e r e a s t h e G r e a t W a ll N o . l e x h ib i t e d s u P e r i o r e o r r o s i o n r e s i s t a n e e . K E Y W O R D S : h o t e o r r o s i o n , c o a t i n g , p l a s m a s p r a y i n g 烟 气轮 机 实际运 行 中遇 到 的是 冲蚀 一 低 温热 蚀 交互作 用 问题 〔 ’ 二 。 叶 片在烟 气流 中受 到氧化 与腐蚀 , 形成较 疏 松的 腐 蚀产 物 , 它很容 易 被催化剂 硬 质粒子 冲蚀 掉 , 如 此循 环往 复直 至叶 片完全失效 。 因此 , 烟 机叶 片 防护 涂层 的 成分 设计必需 同时 考虑 冲蚀 与低温 热蚀 这两 个 重 要 因素及其交互 作用 。 本 文 重 点 研 究长 城 l 号 ( 用 C 一 l 代 表 ) 新型防 护 涂层 的 抗 热 腐蚀 性能 , 作为 比 较也 引人 了 X 一 4 0 等其 它 涂层 的有 关性 能 。 1 实验方 法 1 9 92 一 0 6 一 1 7 收稿 . 材料科学 与工 程系( D e p a r tzn e n t o f M a t e r i a l s S e i e n e e a n d E n g i n e e r i n g ) 第一作者 叶 锐曾 男 6 2 教 授 DOI: 10. 13374 /j . issn1001 -053x. 1993. 01. 022