lization of white cast iron include the following.Most of RE is concen- 有 trated.in sulfide inclusions Fig.3 )which can serve as the substrate for the.crystallization of primary austenite and thus volumetric nucleation of austenite is effected Fig.4 )When crystallized in RE enriched melt,the order of austenitic dendrite axis can be increased thru the effect of constitu- tional undercooling(Fig.5).Both effects cause obstruction to the continuous growth of cutectic carbide.RE modification causes the lowering of eutectic freezing temperature which favors the growth of divorced auste nite-carbide eutectic(fig.6)and it alsc enlarges the eutectic freezing temperature range, favoring volumetric nucleation of eutectics.(Fig.7).Selective absorption of RE on eutectic carbide obstructs the continuous preferential edgewise growth of carbide and favors its more or less uniform growth in different directions as platelike carbide. Based on the above assumption of RE modification mechanism,the effect of RE modification can be improved by the following techniques.Lowering of C content causes the lowering of carbide content and the incresing of prim- ary austenite in white iron(Fig.8 )Slight increase of Si content causes the lowering of eutectic freezing temperature.Inoculation treatment before RE modification can help nucleate primary austenite,which is called duplex trea- tment.Use of complex inoculant and complex modifier can develop their advantageous effects with less unfavorable by effects.with this duplex modi- fication technology,better and more reproducible results of changing carbide morphology in low alloy white cast iron can be obtained with much less RE modifier addition Fig.9). Key words:rare carth,modification.white cast iron 前 言 低合金马氏体白口铸铁目前已发展成为重要的抗磨材料，用子制做各类碾轧辊和矿 山，电力、建材及机械等各个工业部门使用的物料研磨破碎和传送设备中的易磨件，代 替传统使用的钢缺材料，使它的使用寿命提高几倍，经济效益显著。但由于其组织是连 续的脆性碳化物(M:C)基底上分布着奥氏体的转变产物，所以当白口铸铁承受较大的应 力时，裂纹极易在碳化物及金属基体组织的界面上萌生并且容易沿脆性碳化物扩展。这 就妨碍了白口铸铁在冲击载荷较大的条件下应用，而且也影响材料的抗磨性。白口铸铁 的抗磨性随其断裂韧性的增加而增加。目前改善白口铸铁中碳化物的形貌及分布已成为 抗磨白口铸铁研究的焦点。 采用高合金化可以使白口铸铁的碳化物由MC型变为M,C3型（如在高铬白口铁） 23招 ‘ 曰明 陀 幼咖 吐 砂 妞止 一 诚 以触 们魂 纽 以 一 饭 认 ， 珍 一 仁汀 玩 一 讹 急俪 仕 即 砂。 比 ， “ 。 茗 扬恤 廿 还君 烤 恳 卜 “ 印 亡 。 七 长。 记 。 是 加 忱 “ 叱 掀 料 一 扒 价 仇 沙 “ 时 一 比 馆 ‘ “ 让 砰 州 “ 群 一 “ 卿 鱿 “ 盯 ， ，。 叶 卜 “ ‘ 运 时 。 二 呈 嘛 覃硬 及 一 ， 。 卜 交 “ “ “ 麦 “ 士 主 · · ” ， “ 笼。 “ 一 至 ” 功 · 扭 卜 亡 ， 翻 “ 呷 沙 爪卿熙必。 分操。 蒸答淤蒸照洲麟 前 言 翩别 ，种 胭暇分 低合金马氏体 白日 铸铁 目前已发 展 成为重要的抗磨 材料 ， 用 于制做各类碾轧辊 和矿 吓 电方 、 建材及机械等 各个工业部 门使用 的物料研 磨破碎和传送设备 中的易磨件 ， 代 粼 的抗磨 性随 蒸 其断裂 祺 韧性的 增加 蒸 而增加 。羚 目前改善 斌 白口铸铁熬中碳化物 的 形貌瀚及分布 已成为 抗磨 白口 铸铁研究 的焦点 。 采用高合金化可以 使白 口铸铁的碳化物 由 。 型变为 ， 。 型 如在高铬白口铁