D0I:10.13374/j.issn1001-053x.1987.04.005 北京钢铁学院学报 第9卷第4期 Journal of Beijing University Vol,9 No.4 1987年10月 of Iron and Steel Technology Oct.1987 无钴马氏体时效合金 任怀亮何肇基王学诚，张葵 （金相教研室) 摘 要 对含铜无钴马氏体时效合金系列进行了研究，固溶处理时第2相F。:Mo完全 溶解的温度不能低于950℃，含铝量为≤6%的合金，高温逆转奥氏体再结晶处理温 度为950℃；含钼量大于6%的合金，再结晶处理的温度，随钼含量增加而提高。 再结品的光学显微组织显长方块状，未再结晶的光学显微组织呈细条束状。540℃ 时效处理，主要沉淀相为Ni3Mo和FeMo,前者为棒状，后者是圆点状.Fe-Ni15 Mo6-Cu1-Ti合金，经950℃弼溶和再结品处理，540℃时效3，常规力学性能相当 于18Ni(250)的水平， 关键词：马氏体时效合金，固溶处理，再结品，逆转奥氏体 Cobalt-Free Maraging Alloys Ren Huailiag He Zaoji Wang Xuechang Zhang Kui Abstract The maraging alloys series containing copper but cobalt free have been investigated.It was found that during solid solution treatment,the temperature for the second phase Fe2Mo dissolving completcly could not lower than 950 C,and for the alloys containing 6 Mo or less,the rec- rystallization treatment temperaturc for high temperature reversed auste- nite was 950 C.For the alloys containing more than 6%Mo,the recrys- tallization treatment temperature raised with increasing Mo%.Under opi- tical microscopy the morphology after recrystallization was rectangular block shape while it was fine packet shape before recrystallization. 198610-28收稿 31第 卷第 期 年 月 北 京 钢 铁 学 院 学 报 。 。 ， 无钻马 氏体时效合金 任怀亮 何肇基 王 学诚 ‘ 张 葵 金 相教研室 摘 要 日 矛 对含铜无钻马氏体时效合 金系列进行了研究 固溶处理时第 相 。 完全 溶解的温度不能低于躬。 ℃ 含钥量 为三 书的合金 ，高温逆转奥氏 体再结晶处理温 度为 。 ℃ 含铂量大于 多的合金 ， 再结晶处理的温度 ， 随 铂含量增加而提高 再结晶的光学显微组织 呈长方块状 ， 未再结晶的光学显微组织呈细 条束状 ℃ 时效处理 ， 主要沉淀相为 。 和 。 ， 前者为棒状 ， 后者是 圆点状 。 一 一 卜 合金 ， 经 。 ℃ 固溶和 再结晶处理 ， 。 ℃ 时效 ， 常规力学性能相 当 于 的水平 ， 关链词 马氏体时效合金 ， 固溶处理 ， 再结晶 ， 逆转奥氏体 一 ” ’ 犷 班 夕 夕 夕 ， ℃ ， ，， ， ’ ， 入 收稿 DOI ：10．13374／j ．issn1001－053x．1987．04．005