Vol.24 No.4 张丽娜等：P/M Rene95合金夹杂物微观力学行为观察 ·435· 验中却是大夹杂物处在远低于合金的屈服强度 参考文献 前先产生裂纹. 1 Sims CT,Stoloff N S,Hagel W C,著.赵杰，译.高温 合金一字航和工业动力用的高温材料M.大连： 3结论 大连理工大学出版社，1992 2 Eric S Huron,Paul G Roth.The Influence of Inclusions on 通过特定的试验观察和分析，得到以下结 Low Cycle Fatigue Life in a P/M Nickel-Base Disk 论： Superalloy [C].[In:Proceedings of the Eighth Interna- (1)在SEM原位拉伸试验中，随着载荷的增 tional Symposium on Superalloys,1996.359 加，裂纹在陶瓷夹杂物处萌生 3 Shamblen C E,Chang D R.Effect of Inclusions on LCF Life of HIP Plus Heat Treated Powder Metal Rene95[J]. (2)在原位拉伸过程中，A1,0,夹杂物的尺寸 Metallurgical Transaction B,1985,16B:775 不同，对P/M Rene95合金的开裂影响不同.主 4 Shailesh J Patel,Ian C Elliott.Production of High-Strength 要表现在它们导致裂纹萌生的方式上.小尺寸 P/M Disc Alloys by "Superclean"Cast/Wrought Technol- 的夹杂物引起的裂纹萌生易于产生在夹杂物内 ogy [C].[In:Proceeding of the Seventh International 部，即夹杂物本身开裂，产生裂纹是在基体大面 Symposium on Superalloys,1992.13 积屈服之后；而大夹杂物处的裂纹则是在合金 5 Fu Z M,Au P.Influence of Microstructure on High Tem- perature Low Cycle Fatigue Life in P/M Rene95[C].[In: 基体未屈服之前萌生，位于夹杂/基体的界面. Conference:Mechanical Behavior of Materials-V,1987. (3)P/MRene95中的Al,O,通常呈不规则的 1165 块状存在，有些夹杂物在材料制备过程中被破 6 Barker J F,Van Der Molen E H.Effect of Processing Vari- 碎，A1,O/基体界面呈机械结合状态，使得界面 ables on Powder-Metallurgy Rene95,Superalloys- 易于分离而产生裂纹， Processing[C].[In:Proceedings of the Second Interna- tional Conference,1972.AA:18 7李代锤.钢中的非金属夹杂物M).北京：科学出版社， 致谢：感谢国家自然科学基金资助，感谢美国GE航空 1983 发动机公司提供的PM高温合金材料 SEM In-situ Observation on Behavior of Inclusions with Different Size in P/M Rene95 Superalloy ZHANG Lina,ZHANG Maicang.LI Xiao,DONG Jianxin,XIE Xishan Material Science and Engineering School,UST Beijing.Beijing 100083,China ABSTRACT Special arranged experiments were designed for SEM in-situ observation on inclusion behavior in seeded P/M Rene95 superalloy at tension loading stage.Two different size Al,O,inclusion's behavior were followed by continuous loading till to fracture.Observed results show that crack can be easily initiated at the interface of larger inclusion and matrix even at the stress level lower than yield.Crack can be also initiated in the inclusion and then propagated to the matrix.Both mechanics show the harmful effect of inclusions in P/M superalloys. KEY WORDS P/M Rene95;inclusion;SEM in-situ tension observation;behavior of inclusions】 张丽娜等 舰 合金 夹杂物微观 力学行为观 察 弓 验 中却是大夹杂物处在远低于合金 的屈 服强度 前先产生裂纹 参 考 文 献 结 论 通 过特定 的试验观察 和 分析 ， 得 到 以 下 结 论 在 原位拉伸试验 中 ， 随着载荷 的增 加 ， 裂纹在 陶瓷夹 杂物处萌生 在原位拉伸过程 中 ， ， 夹杂物的尺 寸 不 同 ， 对 合金 的开裂影 响不 同 主 要表现在它们导 致裂纹萌生 的方式上 小尺 寸 的夹杂物引起 的裂纹萌生易于产生 在夹 杂物 内 部 ， 即夹杂物本身开裂 ， 产生 裂纹是在基体大面 积屈 服之后 而 大夹杂物 处 的裂纹则 是在 合金 基体未屈服之前萌生 ， 位于夹杂 基体 的界 面 迎涯 中的 ， 通 常呈 不 规则 的 块状存在 ， 有些夹杂物在材料制备过程 中被破 碎 ， 基体界面呈 机械结合状态 ， 使得界面 易于分离而产生 裂纹 致谢 感谢 国家 自然科学基金资助 ， 感谢美 国 航空 发动机公 司提供的 从 高温合金 材料 工 任 ， 吧 ， 著 赵杰 ， 译 高温 合金－ 宇航和工业动力用 的高温材料 【 大连 大连理工大学 出版社 ， ， 即 一 ， ， ， ， ， 一 ” ，， 扩 七 ， ， 【 一从 ， 自 、 乞 一 ， 』 － ， 李代锤 钢中的非金属夹杂物 北京 科学 出版社 ， 一 从 月叼刀 ， 刁刀 凡白 ， ， ， 火 ， ， ， 一 ， ， 一