·368· 北京科技大学学报 1997:第4期 3结论 (1)在合成立方氮化硼相图上，把V形区的】区做为优晶区与本实验结果符合较好 (2)使用琥珀色催化剂，合成立方氮化硼的温度压力条件都远低于合成金刚石的温度压 力条件， (3)合成立方氨化硼，采用慢超压升温升压方式是有利的. (4)合成立方氮化硼应采用比合成金刚石低的超压速度， 参考文献 1李玉萍，徐晓伟，李湘瑶，武飞.立方氮化硼合成块组装方式的研究.超硬材料与工程，1995(2)：12 2 Onodera A,Inoue K.Synthesis of Cubic Boron Nitride from Rhombedral Form under High Static Pressure.J Mater Sci,1990,25:4279 3 Bocuillon G.Synthesis of Cubic Boron Nitride Using Mg and Pore or M-doped Li,N.Ca,N,and Mg N,with M=Al,B,Si,Ti.J Mater Sci,1993.28:3547 4吉林大学固体物理教研室，人造金刚石.北京：科学出版社，1975.76 Methods of cBN Synthesis under High Pressure and Temperature 亚uping'Xu Xiaowei》Li Xiangyao2)huFe 1)Applied Science School.UST Beijing,Beijing 100083,China 2)Institute of Superhard Materials,Ministry of Metallurgical Industry.Yanjiao.101601 ABSTRACT The influences of temperature,pressure and the elevating pressure speed on the amber cBN synthesis using catalyst have been studied.The results show that,under the experimental conditions,both temperature and pressure for the amber cBN synthesis are belower than these for the diamond synthesis,and the results of cBN synthesis can be improved if the elevating pressure speed is slowed down. KEY WORDS synthesis,catalyst,cubic boron nitride,high temperature and pressure. 3 6 8 . 北 京 科 技 大 学 学 报 19 9 7 第 4期 3 结论 ( )l 在 合成 立方 氮化 硼相 图上 , 把 V 形 区 的 1 区做 为优 晶 区 与本 实验结 果符合 较好 . ( 2) 使 用唬 拍 色催 化剂 , 合 成 立方 氮化 硼 的温 度 压力 条件 都 远低 于 合成 金刚石 的温 度压 力 条件 . (3) 合 成立 方氮 化硼 , 采用 慢超 压 升温 升压方 式是 有利 的 . (4) 合成立 方氮 化硼 应采 用 比合 成 金 刚石低 的超 压速度 . 参 考 文 献 1 李玉萍 , 徐晓伟 , 李湘瑶 , 武飞 . 立方氮化硼合成块组装方式的研究 . 超硬材料 与工程 , 1 9 95 ( 2) : 12 2 O l l od e ar A , I n o ue K . Sy n hte s i s o f C u ib e B o or n 瓦itr de ofr m hR o m be d al oF rm u n d e r 托g h S at it e P r e s s u re . J M a t e r S e i , 1 9 9 0 , 2 5 : 4 2 7 9 3 B oc 山l l o n G · s y n ht e s i s o f C u ib c B o or n 惭itr de sU i n g gM a n d p o re o r M 一 do 详d iL 3 N , C a3 凡 an d gM 3 N , w iht M = lA , B , 5 1 , T i · J M ate r s e i , 19 9 3 , 2 8 : 3 5 4 7 4 吉林大学 固体物理教研室 . 人造金 刚石 . 北京: 科学 出版社 , 19 7 5 . 76 M e ht o d s o f e B N S y n th e s i s u n d e r H i g h P r e s s u r e an d T e m P e r aut r e 百 uYP in g , ) xu ix a o w e i , ) 百 ix a n舒 a o , ) 肋 凡i , ) l ) A P P li e d S e i e cn e S e h o l , U S T B e ij i n g , B e ij i n g 10 0 0 8 3 , C ih n a 2 ) I n s it t u te o f S u pe 比 a 记 M a te ir a l s , 腼 in s tI’y o f M e tal l u rg i e al I n d us try , Y咧i a o , 10 16 0 1 A B S T R A C T T l l e i n fl u e cn e s o f te m pe ar tu re , Per s s u er a n d ht e e l e v a it n g Per s s u er s pe e d o n ht e am be r e B N s y n ht e s i s u s i n g c a at l y s t h va e be e n s ut d i e d . hT e er s u l st s h o w ht a t , u n d e r het e x pe ir m e n at l e o n d iit o n s , bo ht et m pe ar ut er a n d Per s s u er fo r het am be r c B N s y n ht e s i s aer be l o w e r ht a n ht e s e fo r t h e d i am o n d s y n ht e s i s , a dn het er s u lst o f e B N s y n ht e s i s e a n be im P or v e d if ht e e l e v a it n g P er s s u er s pe e d 1 5 s l o w e d d o w n . K E Y W O R D S s y n ht e s i s , c a alt y s t , c u b i e bo r o n in t ir d e , ih g h et m pe ar ut er an d Per s s u er