研究与检测· Research and test echnology of Eliminating Weldline on Products Surface Using Taguchi Methods 应用 Taguchi方法消除产 品表面熔接痕的工艺研究 摘要:为提高注塑产品表面质量,消除产品表面熔接痕,本文利用 Taguchi方法设计了L9实验矩阵, 分析了熔体温度、模具温度、注射压力、保压时间等工艺因素对ABS制品表面熔接痕长度的影响,预测了最佳 工艺参数,并在验证实验中消除了产品表面熔接痕,对注塑生产具有一定的指导意义 关键词:注塑成型熔接痕工艺优化 Taguchi法 Abstract: In order to improve the surface quality of injection molded products, eliminate weld line on the products surface, an L9 experimental matrix is designed using Taguchi method to analyse the technology effects. The influence of melt temperature, mould temperature, injection pressure and packing time on the weld line length of ABS products surface is investigated. The optimal process parameter is predicted, and the weld line of the products surface is eliminated during the evaluation experiment. The results may provide some references for injection molding technology. Key words: injection molding weld line process optimum Taguchi method 编者按:随着生活水平的提高,人们对塑料制品质量提出更高的要求,高光无接痕就是其一,为此 业者开始了许多的试验去消除接痕。作者利用 taguchi方法设计了L9实验矩阵就是其中一种尝试 随 着市场对高光无痕注塑产略,但对塑件的表面质量影响较大。 实验部分 品需求的增大,熔接痕的 目前,国内外多数关于消除熔接 消除再次成为注塑行业关痕的工艺研究,主要是通过测量与分析 材料及设备 注的热点问题。熔接痕是指在制品成型含有熔接痕的注塑试件的拉伸强度,来 ABS:奇美塑胶原料(东莞)有限 过程中,两股以上料流前锋熔体汇合时,确定各种工艺参数对熔接痕的影响程度公司 因前锋面上熔体温度下降,在熔体汇合③。本文为研究熔接痕给注塑产品表面 注塑机:SP108A型,仁兴机械(深 处的制品表面上形成的接缝痕迹,常见质量带来的影响,直接以熔接痕长度为圳)有限公司 的熔接痕种类有热接痕、冷接痕以及由指标进行分析,选用丙烯腈-丁二烯-苯 模温控制设备:课题组自行开 于充模时熔体前沿的“喷泉”式流动或乙烯共聚物(ABS),以车载蓝牙外壳为发的模具温控系统,主要由温度快 壁厚不均引起的熔接痕口。对于无定形例,采用 Taguchi实验设计理论,运用速响应模具、加热与制冷装置及温 脆性塑料如PP、PVC、SAN等而言,熔L(3)正交矩阵进行实验,对熔体温度、度测控装置三部分组成,可使模具温 接痕会使塑件力学性能明显降低,在相模具温度、注射压力、保压时间等工艺度在30℃~160℃内调整,精度可达 同的工艺条件下,熔接痕区的强度是原始条件对ABS制品的影响进行了研究,通±0.5℃ 材料的10%~90%:然而对于无定形韧过优化工艺条件获得优化工艺参数组 性塑料如PC、ABS等,熔接痕对塑件的合,并预测出最小熔接痕长度。最后在 实验产品 力学性能损害较小。在有利的成型条件最优工艺参数下进行实验,消除了产品 选用车载蓝牙表面上壳,零件尺 下,熔接缝对塑件的力学性能影响可以忽表面熔接痕。 寸:82.5mm×40mm×6.5mm,壁厚 C1984-20料物造ineaSTTCScandeacTukeu20osFhi月到tronicPublishinghouse.,Allrightsreserved.htp:/www.cnki.net.en-plastics.aet研究与检测· Research and Test 84 塑料制造 PLASTICS MANUFACTURE 2008年11月刊 www.cn-plastics.net 应用Taguchi方法消除产 品表面熔接痕的工艺研究 文/丁 磊 伍晓宇 李伟荣 梁 雄 摘 要：为提高注塑产品表面质量，消除产品表面熔接痕，本文利用Taguchi方法设计了L9实验矩阵， 分析了熔体温度、模具温度、注射压力、保压时间等工艺因素对ABS制品表面熔接痕长度的影响，预测了最佳 工艺参数，并在验证实验中消除了产品表面熔接痕，对注塑生产具有一定的指导意义。 关键词：注塑成型 熔接痕 工艺优化 Taguchi法 Abstract: In order to improve the surface quality of injection molded products, eliminate weld line on the products surface, an L9 experimental matrix is designed using Taguchi method to analyse the technology effects. The infl uence of melt temperature、mould temperature、injection pressure and packing time on the weld line length of ABS products surface is investigated. The optimal process parameter is predicted, and the weld line of the products surface is eliminated during the evaluation experiment. The results may provide some references for injection molding technology. Key words: injection molding weld line process optimum Taguchi method Technology of Eliminating Weldline on Products Surface Using Taguchi Methods 随着市场对高光无痕注塑产 品需求的增大，熔接痕的 消除再次成为注塑行业关 注的热点问题。熔接痕是指在制品成型 过程中, 两股以上料流前锋熔体汇合时， 因前锋面上熔体温度下降，在熔体汇合 处的制品表面上形成的接缝痕迹，常见 的熔接痕种类有热接痕、冷接痕以及由 于充模时熔体前沿的“喷泉”式流动或 壁厚不均引起的熔接痕[1]。对于无定形 脆性塑料如PP、PVC、SAN等而言, 熔 接痕会使塑件力学性能明显降低，在相 同的工艺条件下,熔接痕区的强度是原始 材料的10%～90%；然而对于无定形韧 性塑料如PC、ABS等,熔接痕对塑件的 力学性能损害较小。在有利的成型条件 下,熔接缝对塑件的力学性能影响可以忽 略，但对塑件的表面质量影响较大[2]。 目前，国内外多数关于消除熔接 痕的工艺研究，主要是通过测量与分析 含有熔接痕的注塑试件的拉伸强度，来 确定各种工艺参数对熔接痕的影响程度 [3]。本文为研究熔接痕给注塑产品表面 质量带来的影响，直接以熔接痕长度为 指标进行分析，选用丙烯腈-丁二烯-苯 乙烯共聚物(ABS)，以车载蓝牙外壳为 例，采用Taguchi实验设计理论，运用 正交矩阵进行实验，对熔体温度、 模具温度、注射压力、保压时间等工艺 条件对ABS制品的影响进行了研究，通 过优化工艺条件获得优化工艺参数组 合，并预测出最小熔接痕长度。最后在 最优工艺参数下进行实验，消除了产品 表面熔接痕。 实验部分 材料及设备 ABS：奇美塑胶原料（东莞）有限 公司； 注塑机：SP108A型，仁兴机械（深 圳）有限公司； 模温控制设备：课题组自行开 发的模具温控系统，主要由温度快 速响应模具、加热与制冷装置及温 度测控装置三部分组成，可使模具温 度在30℃～160℃内调整，精度可达 ±0.5℃。 实验产品 选用车载蓝牙表面上壳，零件尺 寸：82.5mm×40mm×6.5mm，壁厚 编者按：随着生活水平的提高，人们对塑料制品质量提出更高的要求，高光无接痕就是其 一，为此 业者开始了许多的试验去消除接痕。作者利用Taguchi方法设计了L9实验矩阵就是其中一种尝试