D0I:10.13374/j.issn1001-053x.1994.s1.005 第16卷增刊 北京科技大学学报 Vol.16 1994年3月 Journal of University of Science and Technology Beijing Mar.1994 电镀锌生产线导电辊腐蚀 失效原因与机理 张普强吴继勋孟惠民卢燕平任群原金钊 (表面科学与腐蚀工程系) 摘要在实验室模拟生产现场工况条件，通过浸泡实验和电化学方法等，研究了铜和304不 锈钢的魔蚀行为；分析了介质条件（温度、F3+及C~浓度）的影响；特别考虑了间断性的阴 极状态对材料腐蚀的作用。提出了生产线上导电辊产生腐蚀失效的原因和机理。 关键词导电辊，腐蚀，阴极状态 An Investigation to Corrosion Failure of Conductor Rolls in Electrogalovanizing Line Zhang Puqiang Wu Jirun Meng Huimin Lu Yanping Ren Qun Yuan Jinzhao (Dept.of Surface Science and Corrosion Engineering) ABSTRACT The corrosion behavior of Cu and SS304 has been studied by means of the im- mersing test and the elecirochemistry method under the conditions simulating industrial site. The influences of medium condition,particularly periodic cathodic state on material corrosion have been investigated.The reason and mechanism of corrosion failure of the conductor rolls have been proposed. KEY WORDS conductor rolls,corrosion,cathodic state 导电辊是连续电镀锌生产线上的一个关键部件，用以在电镀过程中传导强大的阴极电 流。在使用中发现，铜导电辊在很短的时间（约2周）内表面光洁度就明显下降：304不锈 钢导电辊经过一两个月的使用后表面产生了大量深浅不一的麻坑，因而严重影响了镀锌板 的产量和质量，成为一个亟待解决的问题。 现场检测分析表明，不锈钢导电辊发生了较为严重的局部腐蚀（孔蚀及晶间腐蚀），铜 1993-10-21收稿第一作者男29岁博土讲师第 16 卷增 刊 1 9 94 年 3 月 北 京 科 技 大 J o u r n a l o f U n i v e r s i t y o f S e i e n e e 学 报 T e e h n o l o g y Be i j i n g V o l . 16 M a r . 1 9 9 4 电镀锌生产线导 电辊腐蚀 失效原因与机理 张普 强 吴 继 勋 孟 惠民 卢燕平 任 群 原 金 钊 ( 表面科学与腐蚀工程系 ) 摘 要 在实验 室模 拟生产现场工况条件 , 通过浸泡实验和 电化学方法等 , 研究 了铜和 3 04 不 锈钢 的腐蚀行 为 ; 分析了介质条件 ( 温度 、 F e +3 及 cI 一 浓度 ) 的影响 ; 特别考虑 了间断性 的阴 极状 态对 材料腐蚀的作用 。 提出了生产线上导 电辊产生腐蚀失效的原因 和 机理 。 关 键词 导 电辊 , 腐 蚀 , 阴极 状态 A n I n v e s t ig a t i o n t o C o r r o s i o n F a i l u r e o f C o n d u e t o r R o ll s i n E l e e t r o g a l o v a n i z i n g L i n e Z h a n g P u 叮故n g W u , I ix u n M e n g H u 撒 nI L u Y a n P o g R e n Q u n ( eD p t . o f S u r f a e e cS i e n e e a n d C o r r o s i o n E n g l n e e r i n g ) Y u a n J in z h a o A B S T R A C T T h e e o r r o s i o n b e h a v i o r o f C u a n d 5 5 3 0 4 h a s b e e n s t u d i e d b y m e a n s o f t h e im - m e r s i n g t e s t a n d t h e e l e e毛r 以 、 h e rn i s t r y m e t h o d u n d e r t h e e o n d i t i o n s s im u l a t i n g i n d u s t r i a l s i t e . T h e i n f l u e n e e s o f m e d i u m e o n d i t i o n , p a r t i e u l a r l y p e r i o d i e e a t h od i e s t a t e o n m a t e r i a l e o r r o s i o n h a v e b e e n i n v e s t i g a t e d . T h e r e a s o n a n d m e e h a n i s m o f e o r r o s i o n f a i l u r e o f t h e e o n d u e t o r r o ll s h a v e b e e n P r o P o s e d . K E Y W O R D S e o n d u e t o r r o ll s , e o r r o s i o n , e a t h o d i e s t a t e 导 电辊是连续 电镀锌 生产线上 的一个 关键部件 , 用 以在 电镀 过程 中传 导强 大的阴极 电 流 。 在 使用 中发 现 , 铜 导 电辊在 很短的 时 间 ( 约 2 周 ) 内表 面光 洁度就 明显下 降 ; 3 04 不 锈 钢 导 电辊 经过 一两 个 月的 使用后 表 面产 生 了大 量深 浅 不一 的麻坑 , 因而严 重 影响 了镀锌 板 的产 量和 质量 , 成为一 个 鱼待解决的问题 。 现场 检测 分析 表 明 , 不锈钢 导 电辊 发生 了较 为严 重 的局部 腐蚀 (孔 蚀及晶 间腐蚀 ) , 铜 1 9 9 -3 1 0 一 21 收稿 第一 作者 男 29 岁 博 士 讲师 DOI: 10. 13374 /j . issn1001 -053x. 1994. s1. 005