D0I:10.13374/j.is8m1001053x.1986.03.012 1986年9年 北京钢铁学院学报 NO.3 第3期 Journal of Beijing University Sept.1986 of Iron and Steel Technology 不锈钢裸表面在氯化物溶液中的点腐蚀 朱应扬 王旷朱日彰 张文奇 (腐蚀教研， 摘 要 研究了不锈钢去膜表面在氯化钱介质中的点腐蚀现象，去膜表面发生点蚀的 临界电位低于膜覆盖表面发生点蚀的临界电位，去膜表面的点蚀主要在晶界和夹 杂起源，点蚀形貌是敏锐的条纹状花样，根据作者提出的裸面与氯化物介质反 应步骤模型讨诊了点蚀特征电位的意义以及裸表而点蚀形成的过程， 关键词： 不锈钢，点愤蚀，氯化钠溶液，特征电位， Pitting Corrosion of Fresh Stainless Steel Surface in Chloride Solution Zhu Yingyang Wang Kuang Zho Rizhang Zhang Wenqi Abstract The pitting corrosion of the fresh stainless steel surface have been studied.The pitting critical potential of the fresh surface is lower than that of the surface covered by passive film.The pits on the fresh surface are primarily formed on grain boundaries and on inclusions.The morphol- ogy of pits are sharp streak pattern.According to the model of reaction steps of bare surface with chloride medium proposed by authors,the course in which pits are formed on bare surface and the meaning of pit characte- ristic porentials have been discussed. Key words:stainless steel;pitting corrouion;cbloride aolution; charteristic Potentials 91年 年 第 期 北 京 钢 铁 学 院 学 报 。 不锈钢裸表面在氯化物溶液中的点腐蚀 朱应扬 王 旷 朱 日彰 张文奇 腐蚀教研空 摘 要 研究了不锈钢去膜表面在氯化镁介质 中的点腐蚀现象 。 去膜表 面发生点蚀的 临界电位低于膜覆盖表面发生点蚀的临界电位 。 去膜 表面的 点蚀主要在晶界和夹 杂起源 点蚀形貌是敏锐的条纹状花样 。 根据作者提出的裸 害面与氯化物介质反 应 步骤模型 讨论了点蚀特征 电位的意义以及裸表而 点蚀形成的过程 。 关键词 不诱钢 ， 点腐蚀 ， 氯化钠溶液 ，特征 电位 ， 只 ， “ ’ “ 孟 ， 众 日 DOI ：10．13374／j ．issn1001－053x．1986．03．012