原因正是碳化物的择优内氧化对裂纹生长产生了巨大的促进作用。 除上述外，不同作者对腐蚀一蠕变断裂交互作用还提出了一些可能的机制，将它们 一并列入表2，不再一一赞述。就已有的研究来看，A类作用出现在较强的腐蚀环境 中，如沉积盐的热腐蚀条件下；B类作用则出现在环境腐蚀相对较弱的场合。一般地说， A、B两类作用是相互竞争的，那一种起作用由环境、温度、应力及材料等具体条件决定。 表2环境对高温持久断裂的各种作用机制 Table 2 Different mechanisms of environmental effect on stress rupture Type A:Inducing the SCC B:Affecting the micro process of creep type fracture process fracture Grain boundary cracking Enhanced Bridging and bluntiug of External due to growth stress precipitation cracks;[1] corrosion of corrosion products of brittle Enhanced grain boundary in cracks.1] phase along cavitation due to grain migration of Kirkendall boundary(24] vacancies.[1,13] Wedge type cracking; Enhanced grain boundary C12,21] cavitation due to Internal Weakening of grain internal oxidation of boundary due to grain boundary carbides; corrosion corrosion products Cavity nucleation sites on grain boundary; provided by particles C1,10,22) of corrosion products;1,13] Releasing of sulfer Inhibition of cavitation due to internal due to hindered grain oxidation of boundary sliding by sulfides.〔23) particles of corrosion product8.[1.10.13] Diffusion Reduction of grain Enhanced cavitation of boundary adhesion due to decreased surface environ- due to atoms of energy by sulfur atoms.[27] mental sulfur and oxygen on Species grain boundary.[1] 60原因正是碳 化物的择优内氧化对裂纹生长产生 了巨大 的促进作用 。 除上述 外 ， 不 同作者对腐蚀一蠕变断 裂交互作用还提 出了一些可能的机制 ， 将它们 一并列入表 ， 不再一一赞述 。 就 已有的研究来看 ， 类作用 出现在较强 的 腐 蚀 环 境 中 ， 如沉积盐 的热腐蚀 条件下 类作用则出现在环境腐蚀相对较弱 的场合 。 一般地 说 ， 、 两类 作用是相互竞争 的 ， 那一种起作用 由环境 、 温度 、 应力及材料等具体条件决定 。 表 环境 对高温持久断裂 的各种作用机制 五 叮 ” ’ … “ 一‘·气 ‘ ‘一 …兮 ” ‘ “ 。 〔 〕 〕 住 〔 〕 。 〔 ， 〕 侧日 立 〔 ， 〕 〔 ， ， 〕 〔 〕 ， ， 〔 ， 〕 〔 〕 五 妞 ‘ 宫 ， 杭 。 〔 〕 闷 一 〔 〕