D0I:10.13374/j.issn1001-053x.1988.04.026 北京钢铁学院学报 第10卷第4期 Journal of Beijing University Vol,10 No.4 1988年10月 of Iron and Steel Technology 0ct.1988 GH36合金中MC、VC的界面结构 苗柏和谢锡善 (材料科学与工程系) 拥要使用透射电镜现察了GH36合金中M2,C:、VC碳化物和基体之间的界面结 构，在M2,C,/y的半共格界面上分布有错配位错列，间距约10nm。根据g·b=0判据， 可以确定该位错的Burgers vector b=a/2(110),VC/y的相界面是具有很大点陈 错配度(6=+0.155)的共格界面。最后，从M2C。、VC和基体之间的不同界面结构与 性质付论了以碳化物沉淀为主要强化手段的F基GH36合金的强韧化本质以及如何识别波 纹图(Moire pattern)和界面位错的向题。 关键词高温合金，透射电子显微术，界面，错配，位错；被纹图 Interfacial Structure of M2s Ce/Y and VC/Y in GH36 Superalloys Miao Baihe Xie Xishan ABSTRACT:A TEM study on the interfacial structure of M23 Cs/y and VC/y precipitated in GH36 superalloys was conducted.The misfit dislocation distri- bution has been clearly observed at the semi-coherent interfaces of M23 Co/y, a single array along the broadfaces at both sides with Burgers Vector a/2 <110>y and spaced about 10 nm apart.It has been shown circular strain field constrast around the very fine dispersive vC particles of 3 to 12nm or so in size.In addition,strengthening mechanism of Ma3Cs and VC precipitated in GH36 superalloy,and how to identify the moire pattern or interfacial dislo- cations by TEM,were also discussed. KEY WORDS:superalloys,TEM,interface,mismatching,dislocation;moire pattern 1987一09一09收稿 434第 卷第 期 年 月 北 京 钢 铁 学 院 学 报 。 。 。 合金 中 、 的界面结构 苗柏和 谢锡善 材料 科学 与工 程 系 搁 耍 使用透射电镜观寮了 合金中 、 碳化物和 基体之 间的 界面 结 构 ， 在 ，的半共格界面上分布有错配位错列 ， 间距 约 。 根据 · 二 。 判 据 ， 可 以 确定该位错的 ， 二 ，， ， 的相界面是具有很大点 陈 错 配 度 ‘ 二 。 的 共格界面 。 最后 ， 从 、 和 基体之间的不 同界面结构与 性 质讨论 了 以 碳 化 物 沉淀为 主 要 强 化手段 的 基 合金的强韧化本质以及如何识 别波 纹 图 和 界 面位 错的 向题 。 关趁 词 高温 合金 ， 透射 电子显微术 ， 界面 ， 错配 ， 位错， 波纹 图 过 。 叮 万 汀 ‘ ” 。 一 ‘ ， · 由 了 ， 斑 ‘ ， 一 ， ， ， ， ， 一 ，一 收 稿 DOI ：10．13374／j ．issn1001－053x．1988．04．026