采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和万能拉力试验机,研究了Q235-A带钢氧化铁皮的组织、结构及其开裂行为.结果表明,氧化铁皮的成分主要为Fe3O4、Fe2O3和Fe,含有少量的FeO,氧化层厚度比较均匀,约为10 μm,结构致密且与基体结合较好.拉伸实验表明,随着应变的增加,裂纹条数增加呈先慢,后快,再慢的规律.应变达到0.05%时氧化铁皮开始出现裂纹,当应变在0.08%~0.10%范围内裂纹条数随应变增加非常明显,当应变超过0.10%时裂纹条数增加缓慢,应变超过0.15%时裂纹条数几乎不再增加

High temperature corrosion tests in 75%Na2SO4-25%. NaCl molten salt have been conducted on waspalloy specimens plasma sprayed with Co-Cr-B-Si, Ni-Cr-B-Si-hCr3C2, X-40, X-40 + TiC and Ni/Al + Al2O3 coatings, test coupons were exposed isothermally at 750℃up to 200 h. After the corrosion tests, each sample was examined by OM, SEM and EMPA. It was found that X-40, X-40 + TiC and Ni/Al + Al2O3 were violently corroded by the molten salt due to cracking and spalling of the coatings, whereas Co-Cr-B-Si and Ni-Cr-B-Si + Cr3C2 exhibited superior corrosion resistance, which were thought to be related to the formation of chromium and silicon oxide film. A possible corrosion mechanism had been proposed and it is suggested that the excellent corrosion resistance and high hot-hardness of the two B-Si containing coatings may be of significance for applications in petroleum refining industry as

采用灰色关联分析方法对2Cr13和1Cr18Ni9Ti不锈钢在典型地区12a大气腐蚀和环境因素之间的关联度进行了计算,研究了大气腐蚀影响因素随时间的变化.结果表明,2Cr13和1Cr18Ni9Ti不锈钢大气腐蚀影响因素随时间的变化有所不同.2Cr13不锈钢的初期腐蚀,受相对湿度大于80%的年时数、降雨量、温度和Cl-的影响较大,受SO2影响较小.2Cr13不锈钢的中长期腐蚀,主要受Cl-、SO2、相对湿度大于80%的年时数、平均相对湿度及温度等影响.在各个腐蚀阶段腐蚀速率和各种影响因素的关联度大小次序均在不断变化.1Cr18Ni9Ti不锈钢在发生腐蚀的初期,主要受相对湿度大于80%的年时数、降雨量及降尘等因素影响.随着腐蚀时间的延长,Cl-的作用逐渐上升为主导因素,关联度大小次序趋于稳定

利用热力学软件计算了齿轮钢氧含量与夹杂物成分控制、夹杂物转变条件.结果表明,20CrMoH钢中具有较高塑性的非金属夹杂物成分(质量分数)为:SiO2 0%~10%、Al2O3 22%~55%、CaO 42%~60%、MgO 5%~10%,与之平衡的钢液中铝的质量分数大于0.020%,钙的质量分数大于0.7×10-6,a[O]为0.0005%左右;选择组成为CaO>40%、Al2O3 ≤ 37%、MgO 10%、(% CaO+% MgO)/% SiO2为10、SiO2含量尽量低的渣系,钢中Al2O3、MgO·Al2O3夹杂物可转变为低熔点的钙铝酸盐.试验发现LF和RH精炼结束时钢液T[O]含量均随炉渣碱度增加而降低,采用高Al2O3含量的炉渣对降低T[O]含量有利;精炼过程钢液中夹杂物按\Al2O3系夹杂物→MgO-Al2O3系夹杂物→CaO-MgO-Al2O3系夹杂物\顺序发生转变,其中MgO-Al2O3系夹杂物向CaO-MgO-Al2O3系夹杂物的转变是由外向内逐步进行的,转变速度相对较慢;降低T[O]含量有利于生成较低熔点的CaO-MgO-Al2O3系夹杂物

采用固相法制备新型复合稀土Sc2O3和Y2O3掺杂ZnO-Bi2O3基压敏陶瓷,并对其显微组织和电性能进行了分析.结果表明,复合稀土掺杂可提高压敏陶瓷的综合性能,并明显优于单一稀土掺杂,复合稀土掺杂对压敏陶瓷电性能的影响规律仍遵循单一稀土掺杂对压敏陶瓷电性能的影响规律.新型复合稀土Sc2O3和Y2O3掺杂ZnO-Bi2O3基压敏陶瓷,在相同的Sc2O3掺杂比例下,随Y2O3掺杂量的增加,电位梯度呈增加的趋势;在相同的Y2O3掺杂比例下,随Sc2O3掺杂量的增加,非线性系数呈增加的趋势.当掺杂Sc2O3的摩尔分数为0.12%、Y2O3的摩尔分数为0.20%时,复合稀土掺杂ZnO-Bi2O3基压敏陶瓷的综合电性能最为理想,电位梯度为410 V·mm-1,非线性系数为38.0,漏电流为0.58μA

应用X射线衍射,选区电子衍射和同步X射线衍射等方法,对锂离子电池正极材料Li[Ni1/3Li1/9Mn5/9]O2的结构和充放电行为进行了研究.结果表明Li[Ni1/3Li1/9Mn5/9]O2可标定为单相α-NaFeO2,并具有$\\sqrt 3 $ahex.×$\\sqrt 3 $ahex.×$\\sqrt 3 $chex.超结构特征.电池充电时,伴随锂离子的脱出,相邻氧原子层间的静电斥力逐渐增大,当电压为3.8V时应力达到最大.接近4.6V时,晶胞常数c急剧下降,绝大多数Li+从材料的锂层拔出,Ni2+发生氧化.4.6~4.8V之间c增大,a变化很小,说明过渡金属层中的Li+拔出,而过渡金属离子的氧化状态未改变

使用以稳定的ZrO2为电解质的高温固体电解质电池电动势方法测量了Ni3Ga非整比金属间化合物1073至1273K均相范围内Ga的活度,计算了偏摩尔焓和偏摩尔摘等热力学性质.考虑4种点缺陷,即分别在2个亚晶格上的反结构原子和空位共存于该Ll2型化合物中,各缺陷生成自由能为可调参数:Ef(Aβ)=0.60eV,Ef(Bα)=0.60eV,EfV(α)=1.5eV,EfV(β)=2.0eV,用统计热力学方法推导了Ni3Ga非整比化合物均相范围内缺陷浓度及其与温度和成分的关系,得到1123K时整比处的无序参数α'=0.0009

将齿轮的轧制成形与传统的楔横轧原理相结合,在轧制成形轴类零件的同时实现齿形部分的轧制成形,不仅可以实现齿轮轴零件的近净成形,而且可以提高齿的承载能力及使用寿命.在轧制齿形部分的过程中,对轧件的进给采用分段阶梯式进给方式,轧件在模具的带动下以自由分度方式进行轧制.通过数学模型和实验,给出了轧制各阶段模具齿距的计算方法和变化规律、模具的齿形设计方法、模具对轧件首次分度时最小进给量的计算方法以及轧制各阶段进给量的变化规律.用De-form-3D数值模拟仿真软件模拟轧制过程,在H630轧机上轧制出模数m=2,齿数z=20,压力角a'=20°的齿轮轴上的齿形,实验证明在楔横轧机上轧制齿轮轴上的齿形是可行的

利用自制的油轮舱CO2-O2-H2S-SO2湿气环境腐蚀模拟装置,对Ni和Cu含量不同的三种低合金钢进行了油轮舱湿气腐蚀模拟实验,比较和分析了三种不同成分的低合金钢在模拟原油舱湿气环境中的腐蚀速率、腐蚀形态和腐蚀产物,探讨了油轮舱CO2-O2-H2S-SO2湿气环境中钢的腐蚀机理.结果表明:三种不同成分低合金钢的腐蚀形态均为全面腐蚀,伴随着腐蚀产物的形成和脱离,钢的腐蚀速率随实验时间的延长出现了波动变化;钢中Ni和Cu元素可明显提高钢的耐油轮舱湿气腐蚀性能;在油轮舱湿气环境下,同时存在四种腐蚀性气体CO2-O2-H2S-SO2的析氢和吸氧腐蚀,同时也存在钢表面薄液膜中H2S被O2氧化形成的元素S引起的湿S腐蚀;CO2-O2-H2S-SO2湿气腐蚀减薄量DLt与时间t之间较好地满足指数关系DLt=AtB,并得到合金元素含量不同的三种钢的系数A和指数B的数值

利用扫描电镜(SEM)、透射电镜(TEM)对炉卷轧机生产X100管线钢的显微组织特点进行了观察与分析,通过背散射电子衍射技术(EBSD)探讨了X100管线钢的有效晶粒尺寸与低温韧性的关系,并利用物理化学相分析的方法对X100管线钢的析出粒子尺寸分布和强化作用进行了定量分析.结果表明:X100管线钢的显微组织以粒状贝氏体为主,晶粒内部和晶界上弥散分布着大量细小的马氏体/奥氏体(M/A)岛;X100管线钢的有效晶粒尺寸较小,仅为2μm左右,细化有效晶粒尺寸和降低组织方向性有利于提高管线钢的低温韧性;X100管线钢中的析出粒子尺寸较小,平均尺寸为45.4nm,但由于其总体质量分数只有0.062%,经计算,其析出强化作用约为52MPa,析出强化对屈服强度贡献较小