D0I:10.13374/j.iss1001-053x.1991.05.014 第13卷第5(1)期 北京科技大学学报 Voi.13No,5(1) 1991年9月 Journal of University of Science and Technology Beijing Sept.1991 铝的冷封闭硫酸阳极氧化膜组成 肖珩· 樊自栓·徐源 张文奇 摘要：用超荐切片、透射电镜、扫描电镜、电子能谱和X射线相分析仪分别研究了铝 的硫酸阳极若色氧化膜，在冷封闭制度下的微观组成。结果表明，者色阳极氧化膜在冷封 闭4m血之后，氧化膜的外表面层附近、老面层及深处都存在有封闭材料镍。其相对含量 逐步增大至9.241%：著色材料锡在氧化膜深处达到20.420%；氧化时键合的S042-在冷 封闭时部分祓放出，氧化膜深处的S含量从5%降至3%左右。铝的疏酸阳极氧化膜经100 min冷封闭，仍为非品态物质。 关键词：阳极氧化膜，冷封闭，铝 Components of the Cold Sealed Films on Aluminium Anodired in Sulphuric Acid Xiao Heng'Fan Zishuan.Xu Yuan. Zhang Weiqi ABSTRACT:The micro Components formed anodic films on Al were studied by ultrathin section technology,TEM,SEM etc,The results show that after 4 min of cold sealing,Ni(as a sealing agent)can be found near the outer layer,surface layer and the deep place of the anodic films,Its relative content increases 系 to 9.244%.The content of Tin (as a coloring agent)can reach to 20.42%in the deep places of the films,while the content of s in the same place decreases from about 5%to 3%.After 100 min of cold sealing,the films on Al are still amorphous substance, KEY WORDS:anodic film,cold sealing,Aluminium 1990-06-22收稿 ~表面科学与腐蚀工程系(Department of Surface and Corrosions) 483第畴第 钊 期 北 京 科 技 大 学 学 报 。 。 年 。 月 二 了 ’ 了 。 。 。 一 一 一 一 一 一一 — 一 一 一 一 一 一 ‘ — 一一 一 油 一 一 一 一一 一 一 一 一 一 一 一 一 一 一 一一 一 一 一一 一一 —一 一 一 一 一 一 — 一 一 一 一 一 一 一 一 一一一 一 铝的冷封闭硫酸阳极氧化膜组成 肖 布 ’ 樊 自栓 ‘ 徐 源 ’ 巫互彭 · 摘 要 用超薄切片 、 透射 电镜 、 扫 描 电镜 、 电子能谱和 射 线相 分析仪 分别研究 了铝 的 硫 酸 阳极 着色氧化膜 ， 在冷封 闭 制度下 的微观 组 成 。 结果表明 ， 着 色阳极 氧化膜 在冷封 闭 之 后 ， 氧化 膜 的外表 面 层附 近 、 表面 层及深处都存 在有封 闭材 料镍 。 其相对含 量 逐步 增大 至 “ ， 着 色材料锡 在氧化膜 深处 达 到 氧 化时键 合的 一 在冷 封 闭 时 部分被 放 出 ， 氧化膜 深处的 含量从 降至 左 右 。 铝 的硫 酸 阳 极 氧化膜经 。 。 冷 封 闭 ， 仍为 非晶态物 质 。 关键词 阳极氧化膜 ， 冷封 孔 铝 夕 ， ” ， 五 、 妙 ， ， ， ， 。 寸 吐 。 ， 对 ， 。 ， ， 一 一 收稿 ‘ 表面科学与腐蚀工程 系 。 冬 DOI ：10．13374／j ．issn1001—053x．1991．05．014