第16卷增刊 北京科技大学学报 Vol.16 1994年3月 Journal of University of Science and Technology Beijing Mar.1994 锌镍合金镀层的铬酸盐钝化 卢燕平 何英 孟惠民 张普强 吴继勋 (表面科学与腐蚀工程系) 摘要采用一种新的铬酸盐饨化处理方法，可进一步提高含镍量为12%~13%的锌镍合金 镀层的化学稳定性，其耐蚀性比未钝化的高5倍。研究了铬酸盐溶液成分及操作条件对钝化膜 形成机理的影响，并对膜的耐蚀性与防护机理进行了探讨。 关键词电镀，Zn-Ni合金，转化涂层，铬酸盐 Chromate Passivation of Zn-Ni Alloy Plating Lu Yanping He Ying Meng Huimin Zhang Puqiang Wu Jirun (Dept.of Surface Science and Corrosion Engineening) ABSTRACT The chemical stability of Zn-Ni alloy coating containing 12%~13%Ni is fur- ther improved in this paper by means of a new chromation process and its corrosion resistance is five times higher than unchromation one.The effects of the composition of chromate solu- tion and operation conditions on formed mechanism of conversion coating were investigated, and the protective mechanism of the coating was also discussed. KEY WORDS electrodeposition,Zn-Ni alloy,conversion coating,chromate 从锌基合金镀层对钢铁的防蚀机理和实际耐蚀性测定两方面看，含镍量为10%~15% 的锌镍合金镀层的耐蚀性能最佳)。若将合金经过钝化处理，可进一步明显提高耐蚀性。但 由于镀层中镍含量较高，自发反应能力差，故采用通常铬酸盐钝化处理方法很困难)，且钝 化效果也不理想。因此，本文着重研究钝化液成分和操作条件对钝化膜形成机理的影响，并 对钝化膜的耐蚀性与防护机理进行讨论。 1实验方法 试验用材料采用20g/m2Zn-(12%~13%)Ni合金电镀钢板[]，其尺寸为145mm× 1993-10-28收稿第一作者男48岁副教授第 16 卷增刊 1 9 94 年 3 月 北 京 科 技 大 学 学 报 J o u r n a l o f U n i v e r s i t y o f S e i e n e e a n d T e e h n o l o g y Be i j i n g V o l 。 1 6 M a r . 1 9 9 4 锌镍合金镀层 的铬酸盐钝化 卢燕平 何 英 孟 惠民 张普 强 吴继 勋 (表面科学 与腐蚀 工程 系 ) 摘 要 采用一种新 的铬酸盐钝化 处理方法 , 可进一步提高含镍 量为 12 % 一 13 % 的锌镍 合金 镀层的化学稳定性 , 其耐蚀性 比未钝化 的高 5 倍 。 研究了铬酸盐溶液 成分 及操 作条件对钝 化膜 形成机理 的影响 , 并对膜 的耐蚀性 与防护机理进行了探讨 。 关键词 电镀 , nz 一 iN 合金 , 转化徐层 , 铬酸盐 C h r o m a t e P a s s i v a t i o n o f Z n 一 N i A ll o y P l a t i n g L u aY n Pin g H e y in g M 朋 9 H u lm in Z h an g P uq al n g W u 了拼un ( eD p t . o f S u r f a e e 段 l e n e e a n d C o r r o s 一o n E n g i n e e n 一n g ) A B s T R A C T T h e e h e m i e a l s t a b i li t y o f Z n 一 N i a ll o y e o a t i n g e o n t a i n i n g 1 2 % 一 1 3 % N i 1 5 f u r - t h e r im p r o v e d i n t h i s P a P e r by m e a n s o f a n e w e h r o m a t i o n p r co e s s a n d i t s e o r r o s i o n r e s i s t a n e e 1 5 fi v e t i m e s h ig h e r t h a n u n e h r o m a t i o n o n e . T h e e ff e e t s o f th e e o m p o s i t i o n o f e h r o m a t e s o l u - t i o n a n d o p e r a t i o n e o n d i t i o n s o n f o r m e d m e e h a n i s m o f e o n v e r s i o n e o a t i n g w e r e i n v e s t ig a t e d , a n d t h e p r o t e e t i v e m e e h a n i s m o f t h e e o a t i n g w a s a l s o d i s e u s s e d . K E Y WO R D S e l e e t r od e p o s i t i o n , Z n 一 N i a ll o y , e o n v e r s i o n e o a t i n g , e h r o m a t e 从 锌基 合金 镀层 对钢 铁 的防蚀 机理 和 实际耐 蚀性 测定 两方面看 , 含镍量 为 10 % 一 15 % 的锌镍合金镀 层的耐 蚀性 能 最佳 l[] 。 若将合金经过钝 化处理 , 可进一 步 明显提 高耐 蚀性 。 但 由于镀层 中镍含 量较高 , 自发 反应 能力 差 , 故 采 用通 常铬酸 盐钝 化 处理方 法很 困难川 , 且钝 化效果 也不 理想 。 因此 , 本文 着重 研 究钝化 液成 分和 操作 条件对钝 化膜 形成 机理的影 响 , 并 对钝化膜的耐蚀性与防护 机理 进行 讨论 。 1 实验方法 试验用材料采用 2 09 / m Z Z n 一 ( 12 % 一 13 % ) iN 合金 电镀钢板 阁 , 其尺寸为 1 45 m m x 1 9 9 3 一 10 一 2 8 收稿 第一 作者 男 48 岁 副教 授